等离子喷焊层NiCrBSi+WC/Co的组织与性能

吉林大学学报(工学版) ›› 2011, Vol. 41 ›› Issue (增刊2): 198-201.

等离子喷焊层NiCrBSi+WC/Co的组织与性能

商延赓¹, 王文权², 黄诗铭², 李秀娟¹, 张桂兰¹

1. 吉林大学工程仿生教育部重点实验室, 长春130022;
2. 吉林大学汽车材料教育部重点实验室, 长春130022

收稿日期:2011-01-24 出版日期:2011-09-30 发布日期:2011-09-30
通讯作者: 王文权(1971),男,副教授。研究方向:材料加工。E-mail:wwq@jlu.edu E-mail:wwq@jlu.edu
作者简介:商延赓(1964),男,工程师。研究方向:材料加工。E-mail:shangyangeng@163.com
基金资助:
吉林省科技发展计划项目(20100328,20116006)

Microstructures and properties of plasma surfaced NiCrBSi+WC/Co layers

SHANG Yan-geng¹, WANG Wen-quan², HUANG Shi-ming², LI Xiu-juan¹, ZHANG Gui-lan¹

1. Key Laboratory of Bionic Engineering, Ministry of Education, Jilin University, Changchun 130022, China;
2. Key Laboratory of Automobile Materials, Ministry of Education, Jilin University, Changchun 130022, China

Received:2011-01-24 Online:2011-09-30 Published:2011-09-30

摘要/Abstract

摘要：

利用等离子喷焊技术在H13模具钢表面制备NiCrBSi+20%WC/Co喷焊层。研究表明,基体与喷焊层之间存在明显的分界面,与传统焊接接头的微观组织类似,喷焊层中出现垂直于界面结合方向的柱状晶,这种组织形态在等离子喷涂涂层中从未观察到,说明喷焊层NiCrBSi+20%WC/Co与H13钢基体之间的结合为冶金结合。XRD分析表明,喷焊层中的主要相为γ-(Fe,Ni),Cr₇BC₄,Ni₄B₃,Cr₇C₃和Co₇W₆,并且由于这些相的存在,使得表面喷焊层比H13钢基体具有更高的强度和硬度。

关键词: 材料合成与加工工艺, 等离子喷焊, NiCrBSi+WC/Co, 组织与性能

Abstract:

Microstructures and properties of plasma surfaced NiCrBSi+20%WC/Co layer prepared on the die steel(H13) substrate were investigated.The study showed that the interface boundary existed between the layer and substrate.compared with the typical microstructures of welded joint,the similar columnar grains in the layer perpendicular to the interface line were observed,which were never seen in the plasma sprayed coating.The conclusion could be drawn that the bonding between the NiCrBSi+20%WC/Co layer and H13 substrate belonged to the metallurgical cohesion.The XRD analysis showed that the main phases in the layer includedγ-(Fe,Ni),Cr₇BC₄,Ni₄B₃,Cr₇C₃ and Co₇W₆,which brought higher strength and higher hardness to the surfaced layer than the H13 substrate.

Key words: materials synthesis and processing technology, plasma surfaced layer, NiCrBSi+WC/Co, microstructures and properties

中图分类号:

TG457

商延赓, 王文权, 黄诗铭, 李秀娟, 张桂兰. 等离子喷焊层NiCrBSi+WC/Co的组织与性能[J]. 吉林大学学报(工学版), 2011, 41(增刊2): 198-201.

SHANG Yan-geng, WANG Wen-quan, HUANG Shi-ming, LI Xiu-juan, ZHANG Gui-lan. Microstructures and properties of plasma surfaced NiCrBSi+WC/Co layers[J]. 吉林大学学报(工学版), 2011, 41(增刊2): 198-201.

参考文献

[1] Ahmet T,Cuma B.Characterization of plasma nitrided X32CrMoV33die steel
[J].Materials and Manufacturing Processes,2009,24:898-902.

[2] Pan C G,Wang H C,Zhou J L.Plasma cladding of Ni60-SiC cermet coating on hot forging die
[C]∥2 010International Conference on computing,Control and Industrial Engineering,2010:12-15.

[3] Ivanov V V,Paine I R,Revnyuk P J.Study of thermal fatigue of H13die steel with various surfacet reatments
[J].High Temperature Materials and Processes,2002,21:65-78.

[4] Muhic T,Tusek J,Pleterski M,et al.Problems in repair-welding of duplex-treated tool steels
[J].Metalurgija,2009,48:39-42.

[5] 宋强,仇性启,秦书清.等离子喷焊耐磨涂层制备及性能分析
[J].南京工业大学学报,2009,31(5):102- 105. Song Qiang,Qiu Xing-qi,Qin Shu-qing.Preparationa nd analysis of wear resisting layer by plasma surfacing
[J].Transaction of Nanjin University of Technology,2009,31(5):102-105.

[6] Grum J,Slabe J M.A comparison of tool-repair methods using CO₂ laser surfacing and arc surfacing
[J].Applied Surface Science,2003,208-209:424-431.

[7] Hou Q Y,Gao J S,Zhou F.Microstructure and wear characteristics of cobalt-based alloy deposited by plasma transferred arc weld surfacing
[J].Surfacea nd Coatings Technology,2005,194:238-243.

[8] 龙军峰,孙智富,叶靖.等离子喷焊镍基合金碳化钨复合涂层
[J].重庆工学院学报,2009,23(10):46-49. Long Jun-feng,Sun Zhi-fu,Ye Jing.Ni-matrix alloy and WC composite layer prepared by plasma surfacing
[J].Transaction of Chongqing Institute of Technology,2009,23(10):46-49.

相关文章 15

[1]	姜秋月,杨海峰,檀财旺. 22MnB5超高强钢焊接接头强化性能[J]. 吉林大学学报(工学版), 2018, 48(6): 1806-1810.
[2]	胡志清, 颜庭旭, 李洪杰, 吕振华, 廖伟, 刘庚. 深冷处理对铝合金薄板冲剪成形性能的影响[J]. 吉林大学学报(工学版), 2018, 48(5): 1524-1530.
[3]	邱小明, 王银雪, 姚汉伟, 房雪晴, 邢飞. 基于灰色关联的DP1180/DP590异质点焊接头工艺参数优化[J]. 吉林大学学报(工学版), 2018, 48(4): 1147-1152.
[4]	陈俊甫, 管志平, 杨昌海, 牛晓玲, 姜振涛, 宋玉泉. 金属棒试样拉伸和扭转试验应变范围和力学特性对比[J]. 吉林大学学报(工学版), 2018, 48(4): 1153-1160.
[5]	梁晓波, 蔡中义, 高鹏飞. 夹芯复合板柱面成形的数值模拟及试验[J]. 吉林大学学报(工学版), 2018, 48(3): 828-834.
[6]	刘子武, 李剑峰. 叶片材料FV520B再制造熔覆层冲蚀损伤行为及评价[J]. 吉林大学学报(工学版), 2018, 48(3): 835-844.
[7]	刘纯国, 刘伟东, 邓玉山. 多点冲头主动加载路径对薄板拉形的影响[J]. 吉林大学学报(工学版), 2018, 48(1): 221-228.
[8]	张志强, 刘从豪, 何东野, 李湘吉, 李纪萱. 基于性能梯度分布的硼钢热冲压工艺对形状精度的影响[J]. 吉林大学学报(工学版), 2017, 47(6): 1829-1833.
[9]	吕萌萌, 谷诤巍, 徐虹, 李欣. 超高强度防撞梁热冲压成形工艺优化[J]. 吉林大学学报(工学版), 2017, 47(6): 1834-1841.
[10]	王辉, 周杰, 熊煜, 陶亚平, 向荣. 基于逆向工程的复杂曲面冲压件回弹补偿[J]. 吉林大学学报(工学版), 2017, 47(6): 1842-1847.
[11]	王春生, 邹丽, 杨鑫华. 基于邻域粗糙集的铝合金焊接接头疲劳寿命影响因素分析[J]. 吉林大学学报(工学版), 2017, 47(6): 1848-1853.
[12]	邢海燕, 葛桦, 李思岐, 杨文光, 孙晓军. 基于模糊隶属度最大似然估计的焊缝隐性缺陷磁记忆信号识别[J]. 吉林大学学报(工学版), 2017, 47(6): 1854-1860.
[13]	谷晓燕, 刘亚俊, 孙大千, 徐锋, 孟令山, 高帅. S355钢/6005A铝合金瞬间液相扩散连接接头组织与性能[J]. 吉林大学学报(工学版), 2017, 47(5): 1534-1541.
[14]	谷诤巍, 张文学, 吕萌萌, 王伟, 徐虹, 李欣. 宽翼边U型截面不锈钢型材拉弯成形缺陷控制[J]. 吉林大学学报(工学版), 2017, 47(4): 1165-1170.
[15]	寇淑清, 宋玮峰, 石舟. 36MnVS4连杆裂解加工模拟及缺陷分析[J]. 吉林大学学报(工学版), 2017, 47(3): 861-868.

Metrics

Viewed

Full text

Abstract

Cited

Shared

Discussed