人造石墨与亚稳态再结晶石墨形态变化

吉林大学学报(工学版) ›› 2010, Vol. 40 ›› Issue (01): 87-0091.

人造石墨与亚稳态再结晶石墨形态变化

臧传义¹,郭玮²,胡强¹,黄国锋²,陈孝洲¹,贾晓鹏²

1.河南理工大学材料科学与工程学院|河南焦作 454000；2.吉林大学超硬材料国家重点实验室|长春 130012

收稿日期:2008-04-20 出版日期:2010-01-01 发布日期:2010-01-01
通讯作者: 臧传义（1976-）,男,副教授.研究方向:宝石级金刚石单晶的合成.E-mail:dndzcy@sina.com E-mail:dndzcy@sina.com
作者简介:臧传义（1976-）,男,副教授.研究方向:宝石级金刚石单晶的合成.E-mail:dndzcy@sina.com
基金资助:
国家自然科学基金项目（50172018）；河南省教育厅支持项目（2009A430014）；吉林大学超硬材料国家重点实验室开放课题支持项目（200801）

Morphology changes of synthetic and metastable regrown graphites

ZANG Chuan-yi¹,GUO Wei²,HU Qiang¹,HUANG Guo-feng²,CHEN Xiao-zhou¹,JIA Xiao-peng²

1.Institute of Material Science and Engineering, Henan Polytechnic University, Jiaozuo 454000, China;2.National Key Lab for Superhard Materials, Jilin University, Changchun 130012,China

Received:2008-04-20 Online:2010-01-01 Published:2010-01-01

摘要/Abstract

摘要：

采用人造石墨作为碳源，硼作为添加剂，NiMnCo合金作为触媒，在金刚石稳定区域内（5.4 GPa，1550 K）利用温度梯度法考察了析出的亚稳态再结晶石墨的形态变化情况。结果发现，高温高压下析出的亚稳态再结晶石墨的形态跟所用人造石墨碳源有明显不同，人造石墨主要以杂乱无规则的鳞片状形式存在，而析出的亚稳态再结晶石墨形态较为规则，而且随着添加剂硼的加入，形态发生明显变化。当体系中没有硼存在时，亚稳态再结晶石墨大部分具有规则的六角形状，而且呈现明显的片层状生长模式，晶体垂直立于触媒之中，{0001}面与腔体内的轴向温度梯度方向平行生长；当体系中有硼存在时，亚稳态再结晶石墨形态发生明显变化，呈半球或者圆片状，以螺旋式生长为主，{0001}面与腔体内的轴向温度梯度方向垂直。

关键词: 材料试验, 再结晶石墨, 温度梯度法, 人造石墨, 高温高压

Abstract:

Taking synthetic graphite as the carbon source, boron as the additive, and NiMnCo alloy as the metal solvent, the morphology changes of metastable regrown graphite crystals are studied by temperature gradient method under high pressure and high temperature (HPHT)-diamond-stale pressure and temperature (5.4 GPa, 1550 K). It is found that the morphology of the regrown graphite is obvious different compared with the used synthetic graphite. The synthetic graphite shows an irregular squama-like morphology, but the regrown graphite shows a more-regular morphology. If no boron is present in the system, sheet-like regrown graphite crystals, most with regular hexagonal morphology, stand vertically in the metal solvent, with {0001} facet parallel to the direction of axial temperature gradient. When boron additive is present, regrown graphite crystals, with half-sphere-like or wafer-like morphology, grow in spiral mode, with {0001} face perpendicular to the direction of axial temperature gradient.

Key words: material experiments, regrown graphite, temperature gradient method, synthetic graphite, high pressure and high temperature

中图分类号:

TB39

臧传义,郭玮,胡强,黄国锋,陈孝洲,贾晓鹏. 人造石墨与亚稳态再结晶石墨形态变化[J]. 吉林大学学报(工学版), 2010, 40(01): 87-0091.

ZANG Chuan-yi,GUO Wei,HU Qiang,HUANG Guo-feng,CHEN Xiao-zhou,JIA Xiao-peng. Morphology changes of synthetic and metastable regrown graphites[J]. 吉林大学学报(工学版), 2010, 40(01): 87-0091.

参考文献

相关文章 6

[1]	刘玉艳, 储顺礼, 李男男, 包幸福, 高尚, 沙莉, 胡敏, 蒋引珊. 不同质量比N,O-CMC/n-β-TCP复合材料在模拟体液中的降解性能[J]. 吉林大学学报(工学版), 2013, 43(增刊1): 552-556.
[2]	白志范, 李桂中, 王超, 王良, 张志敏. 高速客车转向架构架焊接接头组织与力学性能[J]. 吉林大学学报(工学版), 2012, 42(增刊1): 207-211.
[3]	宿太超，马红安，朱品文，周林，郭建刚，贾晓鹏 . 高温高压下Bi₂Te₃掺杂PbTe的热电性能[J]. 吉林大学学报(工学版), 2008, 38(01): 66-69.
[4]	臧传义，马红安，黄国锋，贾晓鹏 . 再结晶石墨的形成机制[J]. 吉林大学学报(工学版), 2007, 37(05): 1097-1100.
[5]	臧传义，马红安，田宇，肖宏宇，贾晓鹏. 利用不同籽晶面生长优质宝石级金刚石单晶[J]. 吉林大学学报(工学版), 2006, 36(01): 10-0013.
[6]	张东兴, 吴思刚, 马冰, 赵景海. CFRC抗弯试件的灵敏度[J]. 吉林大学学报(工学版), 2004, (4): 679-683.

Metrics

Viewed

Full text

Abstract

Cited

Shared

Discussed