Fabrication of IR AgCl Single Crystal Fiber

ZHONG Hong-jie1, WANG Yi-ding2   

  1. 1. Department of Physics, Tianjin Institute of Technology, Tianjin 300160, P.R.China;2. State Key Laboratory on Integrated Optoelectronics, Jilin University, Changchun 130023, P.R.China
  • Received:2001-09-12 Revised:1900-01-01 Online:2002-01-26 Published:2002-01-26
  • Contact: ZHONG Hong-jie

摘要: 利用直接成型法技术研制AgCl等单晶光纤, 光纤直径分别为10 μm, 150 μm和300 μm, 长度为40~105 cm. 探讨单晶光纤生长条件, 并讨论产生光纤缺陷的原因.

关键词: AgCl, 单晶, 红外, 光纤

Abstract: This paper deals with direct-formed growth(DFG) technique. Single crystal AgCl fibers were produced by the DFG technique. The diameters of those fibers are 10 μm, 150 μm and 300 μm and their length are 40~105 cm, respectively. The growth conditions of single crystal fibers are explored and the reason of causing fiber defect are discussed.

Key words: AgCl, single crystal, infrared, fiber