金铜精矿中性催化加压浸出预处理工艺

J4 ›› 2011, Vol. 41 ›› Issue (4): 1186-1191.

金铜精矿中性催化加压浸出预处理工艺

李滦宁¹|梁宏伟¹|赵淑杰¹|刘娟丽²|陈博¹|王岚¹|崔玉果³|于长江³

1.吉林大学化学学院|长春130026;
2.西北民族大学化工学院|兰州730030;
3.吉林集安利源黄金有限责任公司|吉林　集安134211

收稿日期:2010-10-11 出版日期:2011-07-26 发布日期:2011-07-26
通讯作者: 梁宏伟（1967-），男，河南驻马店人，副教授，主要从事无机材料方面的研究 E-mail:lianghw@jlu.edu.cn
作者简介:李滦宁(1952-)|女|河北滦县人|教授|主要从事湿法冶金研究,E-mail:luanningli-628@163.com
基金资助:
吉林省科学技术厅项目（20000124）；吉林省校企合作项目；集安市利源黄金有限责任公司项目

Pretreatment Process Technology of Neutral Catalytic Pressure Leaching in Gold and Copper Concentrates

LI Luan-ning¹,LIANG Hong-wei¹, ZHAO Shu-jie¹,LIU Juan-li²,CHEN Bo¹,WANG Lan¹,CUI Yu-guo³,YU Chang-jiang³

1.College of Chemistry, Jilin University, Changchun130026, China;
2.College of Chemical Technology,Northwest University for Nationalities, Lanzhou730030, China;
3.Jilin Ji’an Li’yuan Gold Co.,Ltd, Ji’an134211,Jilin|China

Received:2010-10-11 Online:2011-07-26 Published:2011-07-26

摘要/Abstract

摘要：

针对金铜精矿采用中性催化加压预处理工艺，经试验，在温度180 ℃、氧分压1.8 MPa、催化剂0.14 mol/L的基本条件下，Cu浸出率为99.4%，浸液中残留∑Fe质量浓度仅为3.52 g/L，对后续回收Cu的精炼工艺非常有利。氧化渣以氯化浸金工艺浸出Au、Ag，浸出率分别为98.2%、90.3%，有价元素回收率高，工艺简单，环境效益好。

关键词: 金铜精矿, 中性催化加压浸出, 预处理

Abstract:

The pretreatment method based on catalytic pressure in neutral conditions was used for leaching gold and copper concentrates. The results suggested that 99.4% of Cu could be leached out from gold and copper concentrates when temperature was 180℃, partial pressure of oxygen was 1.8 MPa and amount of catalyst was 0.14 mol/L. The total of Fe was only 3.52 g/L in leachate, which was beneficial to recovery of Cu in the follow-up process. In the residue, 98.2% of Au and 90.3% of Ag could be leached out by chloride leaching gold process. The pretreatment process was straightforward and the environmental benefits.

Key words: gold and copper concentrates, neutral catalytic pressure leaching, pretreatment process

中图分类号:

TF803.21

李滦宁, 梁宏伟, 赵淑杰, 刘娟丽, 陈博, 王岚, 崔玉果, 于长江. 金铜精矿中性催化加压浸出预处理工艺[J]. J4, 2011, 41(4): 1186-1191.

LI Luan-ning, LIANG Hong-wei, ZHAO Shu-jie, LIU Juan-li, CHEN Bo, WANG Lan, CUI Yu-guo, YU Chang-jiang. Pretreatment Process Technology of Neutral Catalytic Pressure Leaching in Gold and Copper Concentrates[J]. J4, 2011, 41(4): 1186-1191.

参考文献

Metrics

Viewed

Full text

Abstract

Cited

Shared

Discussed