Journal of Jilin University(Earth Science Edition) ›› 2020, Vol. 50 ›› Issue (1): 234-242.doi: 10.13278/j.cnki.jjuese.20180302

Previous Articles    

Effect of Reduced Graphene Oxide Composite Method on Electron Transport Performance of Ag-TiO2 Based Photoelectrodes

Dong Shuangshi1, Fu Shaozhu1, Yu Yang2, Li Chaoqun1, Chu Yicong2   

  1. 1. Key Lab of Groundwater Resources and Environment(Jilin University), Ministry of Education, Changchun 130021, China;
    2. School of Environment, Northeast Normal University, Changchun 130117, China
  • Received:2019-04-25 Published:2020-02-11
  • Supported by:
    Supported by National Natural Science Foundation of China (51678270)

PDF (PC)

271

Abstract: The reduced graphene oxide (rGO) doped and Ag-TiO2 based photoelectrodes were prepared to study the effect of the composite method on the electron transport and tetracycline degradation by photocatalyst. The electrodes were characterized by electrochemical impedance spectroscopy and Mott-Schottky curve. The results showed that the interface resistance of the double-layer/thin film was reduced by the layered composite method on the surface of the carrier; while the total charge transfer resistance was mainly reduced by the fully mixed composite method. In addition, the concentration of the electron donor increased with the increasing of composite amount. When the rGO mass fraction was 0.45% and 0.25%, the degradation rate of tetracycline by the layered composite and the fully mixed doped electrode was 11.4% and 2.3% higher than that of Ag-TiO2, respectively. Under the applied 0.5 V bias voltage, the LG6 degradation efficiency of the layered composite electrode was increased by 5.3%; while the MG2 efficiency of the fully mixed composite electrode was not improved. The layered composite method can improve the electron transport efficiency more effectively on the surface of photocatalyst.

Key words: reduced graphene oxide, photocatalysis, Ag-TiO2, composite method, tetracycline hydrochloride

CLC Number: 

  • X522
[1] Konstantinou I K, Albanis T A. TiO2-Assisted Photocatalytic Degradation of Azo Dyes in Aqueous Solution:Kinetic and Mechanistic Investigations[J]. Applied Catalysis B:Environmental, 2004, 49(1):1-14.
[2] Xue J, Shen Q, Liang W, et al. Controlled Synthesis of Coaxial Core-Shell TiO2/Cu2O Heterostructures by Electrochemical Method and Their Photoelectrochemical Properties[J]. Materials Letters, 2013, 92:239-242.
[3] Deng B, Fu S, Zhang Y, et al. Simultaneous Pollutant Degradation and Power Generation in Visible-Light Responsive Photocatalytic Fuel Cell with an Ag-TiO2 Loaded Photoanode[J]. Nano-Structures & Nano-Objects, 2018, 15:167-172.
[4] Ma Y, Xiong H, Zhao Z, et al. Model-Based Evaluation of Tetracycline Hydrochloride Removal and Mineralization in an Intimately Coupled Photocatalysis and Biodegradation Reactor[J]. Chemical Engineering Journal, 2018, 351:967-975.
[5] 陈宇溪,罗力莎,时峥,等. Ag掺杂型TiO2粉末光催化降解四环素类抗生素废水[J]. 科技创新与应用, 2018, 7(13):36-38. Chen Yuxi, Luo Lisha, Shi Zheng, et al. Photocatalytic Degradation of Tetracycline Antibiotic Wastewater by Ag-Doped TiO2 Powder[J]. Technology Innovation and Application, 2018, 7(13):36-38.
[6] Bolotin K I, Sikes K J, Jiang Z, et al. Ultrahigh Electron Mobility in Suspended Graphene[J]. Solid State Communications, 2008, 146(9/10):351-355.
[7] Park S, Ruoff R S. Chemical Methods for the Production of Graphenes[J]. Nature Nanotechnology, 2009, 4(4):217.
[8] Gadgil B, Damlin P, Kvarnström C. Graphene vs Reduced Graphene Oxide:A Comparative Study of Graphene-Based Nanoplatforms on Electrochromic Switching Kinetics[J]. Carbon, 2016, 96:377-381.
[9] Wang P, Tang Y, Dong Z, et al. Ag-AgBr/TiO2/RGO Nanocomposite for Visible-Light Photocatalytic Degradation of Penicillin G[J]. Journal of Materials Chemistry:A, 2013, 1(15):4718-4727.
[10] Wei S, Wu R, Jian J, et al. Graphene Oxide/Core-Shell Structured TiO2@TiO2-x Nanocomposites with Highly Efficient Visible-Light Photocatalytic Performance[J]. RSC Advances, 2015, 5:40348-40351.
[11] Lee J H, Kim I K, Cho D, et al. Photocatalytic Performance of Graphene/Ag/TiO2 Hybrid Nanocomposites[J]. Carbon Letters, 2015, 16(4):247-254.
[12] Li G, Wang T, Zhu, Y, et al. Preparation and Photoelectrochemical Performance of Ag/Graphene/TiO2 Composite Film[J]. Applied Surface Science, 2011, 257(15):6568-6572.
[13] Lee M S, Hong S-S, Mohseni M. Synthesis of Photocatalytic Nanosized TiO2-Ag Particles with Sol-Gel Method Using Reduction Agent[J]. Journal of Molecular Catalysis A:Chemical, 2005, 242(1/2):135-140.
[14] Xie Y, Meng Y. SERS Performance of Graphene Oxide Decorated Silver Nanoparticle/Titania Nanotube Array[J]. RSC Advance, 2014, 4:41734-41743.
[15] 朱遂一,霍明昕,杨霞,等.制备多孔镍负载TiO2薄膜光催化降解喹啉和化工废水[J].吉林大学学报(地球科学版),2012, 42(4):1151-1158. Zhu Suiyi, Huo Mingxin, Yang Xia, et al. Preparation of P-25 Films Immobilized on Porous Nickel and High Photocatalytic for the Degradation of Quinoline and Chemical Wastewater[J]. Journal of Jilin University (Earth Science Edition), 2012, 42(4):1151-1158.
[16] Zhang Hao, Lü Xiaojun, Li Yueming, et al. P25 Graphene Composite as a High Performance Photocatalyst[J]. ACS Nano, 2010, 4(1):380-386.
[17] 袁志军.分光光度法测定四环素片中四环素的含量探究[J]. 中国现代药物应用,2011, 5(5):101-102. Yuan Zhijun. Determination of Tetracycline in Tetracycline Tablets by Spectrophotometry[J]. Chinese Journal of Modern Drug Application, 2011, 5(5):101-102
[18] Hou Y, Gan Y, Yu Z, et al. Solar Promoted Azo Dye Degradation and Energy Production in the Bio-Photoelectrochemical System with a g-C3N4/BiOBr Heterojunction Photocathode[J]. Journal of Power Sources, 2017, 371:26-32.
[19] Ding Jie, Bu Yunfei, Ou Man, et al. Facile Decoration of Carbon Fibers with Ag Nanoparticles for Adsorption and Photocatalytic Reduction of CO2[J]. Applied Catalysis B:Environmental, 2017, 202:314-325.
[20] Yang J, Liao W, Liu Y, et al. Degradation of Rhodamine B Using a Visible-Light Driven Photocatalytic Fuel Cell[J]. Electrochimica Acta, 2014, 144:7-15.
[21] Li K, He Y, Xu Y, et al. Degradation of Rhodamine B Using an Unconventional Graded Photoelectrode with Wedge Structure[J]. Environmental Science & Technology, 2011, 45(17):7401-7407.
[22] Aïnouche L, Hamadou L, Kadri A, et al. Interfacial Barrier Layer Properties of Three Generations of TiO2 Nanotube Arrays[J]. Electrochimica Acta, 2014, 133:597-609.
[23] Sun C, Wang Y, Su Q, et al. The Impacts of Graphene Concentration and Thickness on the Photocatalytic Performance of Bi12TiO20/Graphene Composite Thin Films[J]. Materials Research Express, 2017, 4(8):1-7.
[24] 邹东雷,李婷婷,高梦薇,等. 基于响应面的可见光催化材料制备与优化[J].吉林大学学报(地球科学版),2015, 45(6):1833-1838. Zou Donglei, Li Tingting, Gao Mengwei, et al.Preparation and Optimization of the Photocatalytic Materials Under Visible Light with Response Surface Methodology[J]. Journal of Jilin University (Earth Science Edition), 2015, 45(6):1833-1838.
[25] 许颖蘅,应迪文,江璇,等. 光催化燃料电池不同二氧化钛光阳极性能的对比[J]. 环境化学,2016, 15(1):82-88. Xu Yingheng, Ying Diwen, Jiang Xuan, et al. Comparison of Different TiO2 Photoanodes in Photocatalytic Fuel Cells[J]. Environmental Chemistry, 2016, 15(1):82-88.
[1] ZHU Sui-yi, HUO Ming-xin, YANG Xia, QU Hai-li, SHAO Chun-yan, BIAN De-jun, DONG Long, SUN Hong-wei. Preparation of P-25 Films Immobilized on Porous Nickel and High Photoca-talytic Activity for the Degradation of Quinoline and Chemical Wastewater [J]. J4, 2012, 42(4): 1151-1158.
[2] ZHU Sui-yi, HUO Ming-xin, YANG Xia, DONG Long, WANG Jian, JIN Sheng-wei, LIU Xiu. Photocatalytic Degradation of Quinoline in Aqueous Solution by P-25 Film Coated on Foam Nickel Substrate [J]. J4, 2011, 41(5): 1554-1561.
[3] LI Na, XU Zi-li, YU Lian-xiang，WANG Xiao,LI Wen-yan, LIU Xing-juan, DU Yao-guo. Effects of Gas-phase Photocatalytic Oxidation of C7H8 （Toluene）-SO2 on Nano-TiO2/SiO2 [J]. J4, 2007, 37(1): 153-0157.
[4] MU Bai-lin，LI Fang-fei,HOU Tian-yi,SUN Shen-mei,WANG Ying-wei,ZU Sheng-nan. Effect of Natural Zeolite Supports for Photoactive TiO2 During the Photodegradation Process [J]. J4, 2006, 36(04): 668-672.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
Copyright © Journal of Jilin University(Earth Science Edition), All Rights Reserved.
Tel: +86-431-88502374；13756165364　E-mail: xuebao1956@jlu.edu.cn
Powered by Beijing Magtech Co. Ltd