CFRC抗弯试件的灵敏度

摘要/Abstract

摘要： 对CFRC抗弯试件进行了试验分析,探讨了不同载荷工况下CFRC抗弯试件的电阻变化规律。结果表明:CFRC抗弯试件上层电阻随载荷的增加先减小后增大,下层电阻随载荷的增加而增大;在重复载荷作用下,CFRC抗弯试件受拉区电阻不断增大,受压区电阻先减小后增大,残余电阻的存在反映了试件内部存在损伤和损伤积累;在交变载荷作用下,碳纤维混凝土试件的电阻随着载荷周期次数的增加而增大,直至破坏;试件电极形式不同,电阻变化规律也不同。

关键词: 材料试验, 碳纤维增强混凝土, 拉敏性, 电阻

Abstract: Beam test of carbon fiber reinforced concrete(CFRC) was done. vaviation rule of electric resistance of CFRC bending specimen under different loading conditions was discussed. The results show that the upper electric resistance of CFRC bending specimen decreases and then increases as loading became larger, but lower electric resistance decreases gradually. Under repeated loading, the electric resistance of tensile region concrete increases continually, but that of compressive region concrete firstly decreases and then increases. The residual electric resistance reflects inner damage and its accumulation of CFRC specimen. Under alternative loading, the electric resistance of CFRC increases as loading cycle prolongs, until the specimen is damaged. The variation rule of electric resistance depends on the electric pole mode.

Key words: material experiments, carbon fiber reinforced concrete, drawing-sensibility, resistance

中图分类号:

O343

张东兴, 吴思刚, 马冰, 赵景海. CFRC抗弯试件的灵敏度[J]. 吉林大学学报(工学版), 2004, (4): 679-683.

ZHANG Dongxing, WU Sigang, MA Bing, ZHAO Jinghai. Sensitivities of carbon fiber reinforced concrete under bending loading[J]. 吉林大学学报(工学版), 2004, (4): 679-683.

参考文献

[1] CHEN Puwoei, CHUNG D D L. Carbon fiber reinforced concrete for smart structures capable of non-destructive flow detection［J］. Smart Mater Struct, 1993(2):20-30.
[2] PARK Seung Bum, LEE B I. Mechanical prosperities and applications of CFRC composites［J］. High Temperature-High Pressure, 1990,22:663-670.
[3] 张跃,职任涛,朱逢吾,肖纪美.碳纤维(LCF)-无宏观缺陷(MDF)水泥基复合材料电学性能的研究［J］.材料科学, 1992(8):357-361.ZHANG Yue, ZHI Rentao, ZHU Fengwu, XIAO Jimei. Research on the electrical property of carbon fibre-macro deficiency cement matrix composites［J］. Mater Science, 1992(8):357-361.
[4] 毛超照,赵斌元,沈大荣,李卓球. 不同压力作用下压敏水泥试块的电阻变化［C］∥95国家自然科学基金智能材料研讨会文集, 1998:35-40.MAO Chaozhao, ZHAO Binyuan, SHEN Darong, LI Zhuoqiu. Electrical resistance variation of pressure-sensitive cement coupon under different pressure［C］∥Intelligent Material Colloquium of 95 National Nature Science Fund, 1998:35-40.
[5] 姚武, 吴科如. 智能混凝土的研究现状及其发展趋势［J］. 建筑石膏与凝胶材料, 2000(10):22-24.YAO Wu, WU Keru. Present research state and development tendency of intelligent concrete［J］.Construction Gypsum and Gel Material, 2000(10):22-24.
[6] KIM T J, PARK C K.Flexural and tensile strength developments of various shape carbon fiber-reinforced lightweight cementious compo-sites［J］. Cement and Concrete Research, 1998(28):955-960.
[7] 毛起昭, 赵斌元, 沈大荣. 水泥基碳纤维复合材料压敏性的研究［J］. 复合材料学报, 1996,13(4):8-11.MAO Qizhao, ZHAO Binyuan, SHEN Darong. Research on the pressure-sensitive of cement matrix carbon fibre reinforced composites［J］. Acta Materiae Compositae Sinica, 1996,13(4):8-11.
[8] 陈兵,吴科如,姚武.纤维增强混凝土导电性能的研究与应用［J］.混凝土, 2002(7):23-26.CHEN Bing, WU Keru, YAO Wu. Research and application of the electric conduction of fibre reinforced concrete［J］. Concrete, 2002(7):23-26.
[9] 吴科如,陈兵,姚武. 碳纤维机敏水泥基材料性能研究［J］.同济大学学报, 2002,30(4):456-463.WU Keru, CHEN Bing, YAO Wu. Studies on the performance of smart cement matrix carbon fibre reinforced material［J］. Transaction of Tongji University, 2002,30(4):456-463.

相关文章 15

[1]	邱小明, 王银雪, 姚汉伟, 房雪晴, 邢飞. 基于灰色关联的DP1180/DP590异质点焊接头工艺参数优化[J]. 吉林大学学报(工学版), 2018, 48(4): 1147-1152.
[2]	高明亮，于生宝，郑建波，徐畅，张堃，栾卉. PSBP在高密度电阻率法二维反演中的应用[J]. 吉林大学学报(工学版), 2015, 45(6): 2026-2033.
[3]	赵飞翔, 张建伟, 郭孔辉, 张立浩. 基于电阻在线估计的电动助力转向感应电机控制[J]. 吉林大学学报(工学版), 2014, 44(01): 5-10.
[4]	刘玉艳, 储顺礼, 李男男, 包幸福, 高尚, 沙莉, 胡敏, 蒋引珊. 不同质量比N,O-CMC/n-β-TCP复合材料在模拟体液中的降解性能[J]. 吉林大学学报(工学版), 2013, 43(增刊1): 552-556.
[5]	周逢道, 唐红忠, 郭新, 王金玉. 时间域电磁探测发射电流过冲产生原理及抑制[J]. 吉林大学学报(工学版), 2013, 43(04): 1023-1028.
[6]	姜文龙, 贾萍, 汪津, 丁桂英. 基于3-(4-Biphenylyl)-4-phenyl-5-tert-butylphenyl-1,2,4-triazole(TAZ)制备的薄膜电阻的磁效应[J]. 吉林大学学报(工学版), 2013, 43(03): 836-840.
[7]	白志范, 李桂中, 王超, 王良, 张志敏. 高速客车转向架构架焊接接头组织与力学性能[J]. 吉林大学学报(工学版), 2012, 42(增刊1): 207-211.
[8]	徐国成, 徐德生, 赵熹华, 白大成, 陈建和. 弹簧钢电阻点焊接头组织与硬度数值预测[J]. 吉林大学学报(工学版), 2011, 41(02): 377-0381.
[9]	李永强,赵贺,赵熹华,张伟华. 低碳钢激光束电阻缝焊复合焊接中电阻缝焊温度场的数值模拟[J]. 吉林大学学报(工学版), 2010, 40(03): 709-0713.
[10]	臧传义,郭玮,胡强,黄国锋,陈孝洲,贾晓鹏. 人造石墨与亚稳态再结晶石墨形态变化[J]. 吉林大学学报(工学版), 2010, 40(01): 87-0091.
[11]	于生宝，张贤涛，陈天琦，王兆明 . 基于不接触电极的电阻率探测方法[J]. 吉林大学学报(工学版), 2008, 38(02): 370-0373.
[12]	张会平，江中浩，刘先黎，连建设，侯旭峰，李光玉 . 玻璃表面化学镀纳米铜膜[J]. 吉林大学学报(工学版), 2007, 37(01): 11-16.
[13]	陈耕野，叶增平，王元，谷传宏 . 注水电测混凝土的相对渗透系数[J]. 吉林大学学报(工学版), 2006, 36(06): 1019-1024.
[14]	李海波，刘立华，刘梅，郑伟涛. 纳米Fe-Cu体系的结构和电阻温度特性[J]. 吉林大学学报(工学版), 2006, 36(04): 476-479.
[15]	曹海鹏, 赵熹华, 赵贺, 杨黎峰. 人工智能技术在电阻点焊过程控制中的应用与发展[J]. 吉林大学学报(工学版), 2004, (4): 532-537.

Metrics

Viewed

Full text

Abstract

Cited

Shared

Discussed