二氧化硅@裸银纳米颗粒微球制备及其对大肠杆菌活性的影响

吉林大学学报(理学版) ›› 2019, Vol. 57 ›› Issue (04): 985-988.

二氧化硅@裸银纳米颗粒微球制备及其对大肠杆菌活性的影响

沈启慧¹, 单驿轩¹, 刘曼¹, 李冬梅¹, 刘岩¹, 于东冬², 周建光³

1. 吉林化工学院化学与制药工程学院, 吉林吉林 132022; 2. 浙江大学校医院, 杭州 310027;3. 浙江大学工业控制技术国家重点实验室, 智能系统与控制研究所，分析仪器研究中心, 杭州 310058

收稿日期:2018-10-31 出版日期:2019-07-26 发布日期:2019-07-11
通讯作者: 刘岩 E-mail:liuyanjlu@126.com

Preparation of Silica@Bare Silver Nanoparticle Microspheresand Their Effects on Activity of Escherichia coli#br#

SHEN Qihui¹, SHAN Yixuan¹, LIU Man¹, LI Dongmei¹,LIU Yan¹, YU Dongdong², ZHOU Jianguang³#br#

1. Department of Chemistry and Pharmaceutical Engineering, Jilin Institute of Chemical Technology, Jilin 132022, Jilin Province, China; 2. School Hospital of Zhejiang University, Hangzhou 310027, China; 3. Research Center for Analytical Instrumentation, Institute of CyberSystems and Control, State Key Laboratory of Industrial Control Technology, Zhejiang University, Hangzhou 310058, China

Received:2018-10-31 Online:2019-07-26 Published:2019-07-11
Contact: LIU Yan E-mail:liuyanjlu@126.com

摘要/Abstract

摘要： 以SiO₂微球为载体, 利用其表面可自动吸附与还原银离子的能力, 制备新型二氧化硅@银纳米颗粒微球复合材料（SiO₂@Ag NPs）, 并用透射电镜、 Raman光谱、 X射线光电子能谱等对其进行表征, 测试其对大肠杆菌的抑菌性能. 结果表明: 当SiO₂@Ag NPs质量浓度为2.0 mg/mL时, 复合材料的抑菌率为99.8%；当银纳米颗粒表面含有稳定剂聚乙烯吡咯烷酮时, 其抑菌率降低. 表明稳定剂可保护银纳米颗粒的单分散性, 但不利于其抑菌性的发挥.

关键词: 二氧化硅, 裸银纳米颗粒, 抑菌性, 大肠杆菌

Abstract: The silica microspheres were used as carriers to absorb and reduce silver ions automatically on the surface of microspheres, and a new type of composite material of silica@silver nanoparticle microspheres (SiO₂@Ag NPs) was obtained. The silver nanoparticles were characterized by transmission electron microscopy (TEM), Raman spectroscopy and Xray photoelectron s
pectroscopy (XPS), and the bacteriostasis of Escherichia coli was tested. The results show that the antibacterial rate of the composite is 99.8% when the mass concentration of SiO2@Ag NPs is 2.0 mg/mL, and the antibacterial rate decreases when the surface of silver nanoparticles contains stabilizer (polyvinyl pyrrolidone). Therefore, the stabilizer can protect the monodispersity of silver nanoparticles, but it is not conducive to its bacteriostatic effect.

Key words: , silica, bare silver nanoparticle, antibacterial, Escherichia coli

中图分类号:

O614

沈启慧, 单驿轩, 刘曼, 李冬梅, 刘岩, 于东冬, 周建光. 二氧化硅@裸银纳米颗粒微球制备及其对大肠杆菌活性的影响[J]. 吉林大学学报(理学版), 2019, 57(04): 985-988.

SHEN Qihui, SHAN Yixuan, LIU Man, LI Dongmei, LIU Yan, YU Dongdong, ZHOU Jianguang. Preparation of Silica@Bare Silver Nanoparticle Microspheresand Their Effects on Activity of Escherichia coli#br#[J]. Journal of Jilin University Science Edition, 2019, 57(04): 985-988.

[1]	楚刚辉, 姜盼盼. 铜掺杂二氧化硅用于雪菊中木犀草苷的富集及近红外光谱分析[J]. 吉林大学学报(理学版), 2020, 58(4): 1003-1009.
[2]	李晓丹, 姬艳丽, 吴日, 屠培培, 段会坤,尼再中, 王海松, 李淼, 姜苹哲, 李明刚. 大肠杆菌丁醇生产菌的构建及检测[J]. 吉林大学学报(理学版), 2016, 54(02): 391-395.
[3]	郑昆, 杨红, 温刚, 张元新, 葛雅琨, 隋新. 中空介孔二氧化硅纳米材料(HMSNs)的合成及其生物相容性[J]. 吉林大学学报(理学版), 2016, 54(01): 148-151.
[4]	郑昆, 杨红, 葛雅琨, 隋新，温刚, 张元新. 氨基化的介孔二氧化硅纳米材料与pDNA作用[J]. 吉林大学学报(理学版), 2015, 53(06): 1316-1320.
[5]	张晓君, 赵明珠, 赵志海, 于海辉, 周兵. 稻草制浆黑液中木质素/二氧化硅复合材料的制备[J]. 吉林大学学报(理学版), 2015, 53(02): 340-343.
[6]	程东祥, 应海宁, 张玉玲, 金欢驰. 复合二氧化硅气凝胶的制备及去除石油烃效果[J]. 吉林大学学报(理学版), 2014, 52(03): 631-635.
[7]	郑昆, 杨红, 张元新, 葛雅琨, 李世军. 不同粒径高度有序的介孔二氧化硅纳米材料（MSNs）的制备与表征[J]. J4, 2013, 51(03): 510-513.
[8]	苑美荣, 任素霞, 郭玉鹏, 赵旭, 刘艳华. 锐钛矿型TiO₂/SiO₂复合氧化物的制备[J]. J4, 2007, 45(05): 857-860.
[9]	李桂英，邹德生，周立宏，曹玉华. 人细胞周期蛋白D1在大肠杆菌BL21中的表达及纯化[J]. J4, 2006, 44(05): 839-843.
[10]	王群 ,马军，何巍，王晖. 定点突变内皮抑素Zn²⁺的结合位点及突变基因的克隆表达[J]. J4, 2005, 43(01): 106-111.
[11]	景体淞, 徐镜波. 硝基苯对Escherichia coli和Bacillus subtilis生长抑制的构效分析[J]. J4, 2004, 42(01): 130-134.