吉林大学学报(工学版) ›› 2015, Vol. 45 ›› Issue (1): 112-120.doi: 10.13229/j.cnki.jdxbgxb201501017

• Orignal Article • Previous Articles     Next Articles

Corrosion damage of concrete under multi-salt soaking, freezing-thawing and dry-wet cycles

SU Xiao-ping1,WANG Qing2   

  1. 1.School of Civil Engineering, Changchun Institute of Technology, Changchun 130012, China;
    2.College of Construction Engineering, Jilin University, Changchun 130026, China
  • Received:2014-03-26 Online:2015-02-01 Published:2015-02-01

RICH HTML

0   

PDF (PC)

558

Abstract: Experiments are conducted to investigate the damage feature, quality degradation and dynamic elastic modulus decay of concrete under multi-salt soaking, freezing-thawing and dry-wet cycles. Furthermore, the corrosion mechanism of concrete is revealed by electron microscope scanning, analysis of EDX spectrum and chemical composition analysis of the concrete microstructure. Results show that under the common action of multi-salt soaking, freezing-thawing and dry-wet cycles, quality degradation and dynamic elastic modulus decay tend to rise with the increase in the test cycles. The corrosion damage of concrete is mainly caused by the expansion effect of salt crystallization. Combined with the salt chemical erosion, the damage becomes faster and more serious. The total corrosion damage is the result of accumulation of damages caused by a variety of harmful factors.

Key words: structural engineering, salt soaking, freezing-thawing cycle, dry-wet cycle, concrete, corrosion damage

CLC Number: 

  • TU528
[1] Su Xiao-ping, Guo Jin-hui. Study on the durability of fly ash concrete under multi-salt attack and dry-wet cycles[C]∥International Conference on Transportation, 2013: Xianning, China.
[2] Su Xiao-ping, Zhang Li. Comparing tests on the durability of concrete after long-term immersion in different salt solution[C]∥Advances in Civil and Structrual Engineering Ⅲ, the 3rd International Conference on Civil Engineering and Transportation, Kunming, China,2013: 1087-1091.
[3] 宿晓萍,王清. 复合盐与干湿循环双重因素作用下混凝土耐久性试验[J].吉林大学学报:地球科学版,2013,43(3): 851-857.
Su Xiao-ping, Wang Qing. Experiment of the concrete performance under the condition of multiple salts and dry-wet cycles[J]. Journal of Jilin University (Earth Science Edition), 2013, 43(3): 851-857.
[4] 宿晓萍,王清. 盐浸-干湿循环作用后混凝土耐久性对比试验研究[J]. 长春工程学院学报,2012(2):1-4.
Su Xiao-ping, Wang Qing. Comparing experimental study on the concrete performance under the condition of the salt corrosion and dry-wet cycles[J].Journal of Changchun Institute of Technology, 2012(2):1-4.
[5] 宿晓萍. 吉林省西部地区盐渍土环境下混凝土耐久性研究[D]. 长春:吉林大学建设工程学院,2013.
Su Xiao-ping. Research on the concrete durability due to salinized soil in the western region of Jilin province[D]. Changchun: College of Construction Engineering,Jilin University, 2013.
[6] 张静. 吉林省西部地区分散性季冻土的分散机理研究[D]. 长春:吉林大学建设工程学院,2010.
Zhang Jing. Research on the scattered mechanism of dispersion season permafrost in the western of Jilin Province[D]. Changchun: College of Construction Engineering,Jilin University,2010.
[7] 葛勇,杨文萃,袁杰,等. 硫酸盐溶液中混凝土抗冻融干湿循环性能[J]. 东南大学学报,2006, 36(11):234-237.
Ge Yong, Yang Wen-cui, Yuan Jie, et al. Frost-dry-wet resistance of concrete in sodium sulfate solution[J]. Journal of Southeast University,2006, 36(11):234-237.
[8] 田冠飞,冷发光,张仁瑜,等. 盐碱地区土壤对混凝土腐蚀规律和机理的研究[J]. 装备环境工程,2007,10(5):10-22.

Tian Guan-fei, Leng Fa-guang, Zhang Ren-yu, et al. Experimental study of corrosion regularity and mechanism of concrete in alkaline soil[J]. Equipment Environmental Engineering, 2007, 10(5): 10-22.
[9] Winkler E M. Stone:properties, durability in man's envionment[J]. New York: Springer Verlag, 1975: 120.
[10] Erlin B, Stark D C. Identification and occurrence of thaumasite in concrete[J]. Highway Res Rec, 1965 (115):108-113.
[11] Norah C. The occurrence of thaumasite in modern construction-a review[J].Cem Concr Compos, 2002, 24(4): 393-402.
[12] Neil L. A review of the experience of thaumasite sulfate attack by the UK Highways Agency[J].Cem Concr Compos, 2003, 25(8):1051-1058.
[13] 马保国,高小建,何忠茂,等. 混凝土在SO42-和CO32-共同存在下的腐蚀破坏[J]. 硅酸盐学报,2002,32(10):1219-1224.
Ma Bao-guo, Gao Xiao-jian. He Zhong-mao, et al. Corrosion damage of concrete in presence of SO42- and CO32-[J]. Journal of Chinese Ceramic Society, 2002, 32(10): 1219-1224.
[1] SONG Jun, SHI Xue-fei, RUAN Xin. Optimization of thermal parameter identification for mass concrete [J]. Journal of Jilin University(Engineering and Technology Edition), 2018, 48(5): 1418-1425.
[2] DAI Yan, NIE Shao-feng, ZHOU Tian-hua. Finite element analysis of hysteretic behavior of square steel tube confined steel reinforced concrete column steel frame ring beam joint [J]. Journal of Jilin University(Engineering and Technology Edition), 2018, 48(5): 1426-1435.
[3] JI Wen-yu, LI Wang-wang, GUO Min-long, WANG Jue. Experimentation and calculation methods of prestressed RPC-NC composite beam deflection [J]. 吉林大学学报(工学版), 2018, 48(1): 129-136.
[4] WEI Zhi-gang, SHI Cheng-lin, LIU Han-bing, ZHANG Yun-long. Dynamic characteristics of steel-concrete composite simply supported beam under vehicles [J]. 吉林大学学报(工学版), 2017, 47(6): 1744-1752.
[5] LI Jing, WANG Zhe. Mechanical characteristics of concrete under true triaxial loading condition [J]. 吉林大学学报(工学版), 2017, 47(3): 771-777.
[6] YU Tian-lai, LIU Xing-guo, YAO Shuang, Muhammad Mansour. Fatigue performance of RC beams strengthened with externally prestressed CFRP tendons [J]. 吉林大学学报(工学版), 2016, 46(6): 1867-1873.
[7] ZHANG Jing, LIU Xiang-dong. Prediction of concrete strength based on least square support vector machine optimized by chaotic particle swarm optimization [J]. 吉林大学学报(工学版), 2016, 46(4): 1097-1102.
[8] GUO Xue-dong, MA Li-jun, ZHANG Yun-long. Analytical solution of the double joint layer composite beam with shear-slip under vertical concentrated load [J]. 吉林大学学报(工学版), 2016, 46(2): 432-438.
[9] GAO Xiao-jian, SUN Bo-chao, YE Huan, WANG Zi-long. Influence of mineral admixtures on the rheological behavior of self-compacting concrete [J]. 吉林大学学报(工学版), 2016, 46(2): 439-444.
[10] XIAO Xiang, HUANG En-hou, NI Ying-sheng. Theoretical analysis and experiment of the effect of flange width on beam-plates system of prestressed concrete [J]. 吉林大学学报(工学版), 2015, 45(6): 1784-1790.
[11] HOU Zhong-ming, WANG Yuan-qing, XIA He, ZHANG Tian-shen. Simply-supported steel-concrete composite beams under moving load [J]. 吉林大学学报(工学版), 2015, 45(5): 1420-1427.
[12] GAO Xin, WU Xiao-wei, TIAN Jun. Structure of nonlinear finite element model of lightweight aggregate concrete share wall and the factors affecting seismic performance [J]. 吉林大学学报(工学版), 2015, 45(5): 1428-1435.
[13] SU Ying-she, YANG Yuan-yuan. Seismic compression performance of the concrete under high temperature [J]. 吉林大学学报(工学版), 2015, 45(5): 1436-1442.
[14] ZHANG Yan-ling, SUN Tong, HOU Zhong-ming, LI Yun-sheng. Bending-torsion characteristics of steel-concrete curved composite beams stiffened with diaphragms [J]. 吉林大学学报(工学版), 2015, 45(4): 1107-1114.
[15] YE Min, YI Xiao-gang, PU Dong-liang, JIAO Sheng-jie. Global power matching on truck-mounted concrete pump based on genetic algorithm [J]. 吉林大学学报(工学版), 2015, 45(3): 820-828.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
Copyright © Journal of Jilin University(Engineering and Technology Edition), All Rights Reserved.
Tel: +86-431-85095297　Fax: +86-431-85094074　E-mail: xbgxb@jlu.edu.cn
Powered by Beijing Magtech Co. Ltd