High cycle fatigue performance of TRIP automobile steel

YU Yan,ZHANG Xiao-meng,LIU Yun-xu   

  1. Department of Materials, Changchun University of Technology,Changchun 130012, China
  • Received:2013-03-12 Online:2014-09-01 Published:2014-09-01

Abstract: The high cycle fatigue performance of TRIP automobile steel is investigated. First, a series of high cycle fatigue experiments of TRIP steel were conducted. Then, the fatigue limit and fatigue life factor at 800 MPa tensile strength level were studied, and compared with that of DP steel plate at the same strength level. Finally, the microstructure of the fatigue fracture and influence of TRIP effect on the fatigue property of TRIP steel were analyzed. Results show that the TRIP effect improves the fatigue resistance of the steel to some extent. Under the 107 times cycle base condition, the fatigue limit of TRIP steel is obviously higher than that of DP steel, and its fatigue resistance performance is better. The crack source and fatigue area of TRIP steel show obvious ductile fracture characteristics.

Key words: metallic material, TRIP steel, DP steel, fracture scanning, fatigue performance

CLC Number: 

  • TG113
[1] 黄全伟,宋仁伯,周乐育,等. 700 MPa级热轧双相钢的组织和性能[J]. 钢铁研究学报,2009, 21 (8): 21-24.Huang Quan-wei, Song Ren-bo, Zhou Le-yu, et al. Microstructure and property of 700 MPa grade hot rolled dual phase steel[J]. Journal of Iron and Steel Research, 2009,21 (8): 21-24.
[2] Wang X D, Huang B X. The design and characterization of microalloying high strength TRIP steels[J].Metall Mater Trans A, 2008, 39A: 127-129.
[3] 韩志勇,李奉伟,何才,等.车身用不同残余变形的冷轧钢板疲劳性能研究[J].材料应用, 2010(8):46-48.Han Zhi-yong, Li Feng-wei, He cai, et al. Research on fatigue property of body made of cold-rolled steel sheet with different residual deformation[J]. Automobile Technology & Material, 2010(8):46-48.
[4] Zhang Ji-cheng, Fu Ren-yu, Zhang Mei,et al. Bake hardening behavior of TRIP and DP steels[J].Journal of University of Science and Technology Beijing,2008,15(2):132-137.
[5] 孙茂才.金属力学性能[M].哈尔滨:哈尔滨工业大学出版社, 2010:172-179.
[6] 居殿春,竺培显,颜慧成,等.残余奥氏体对TRIP钢机械性能的影响[J]. 冶金丛刊,2008(2):174-177.Ju Dian-chun, Zhu Pei-xian, Yan Hui-cheng, et al. Influnce of retained austenite on the mechanical properties of TRIP steels[J]. Metallurgical Collections, 2008(2):174-177.
[7] 刘强,江海涛,唐荻,等. TRIP钢中残余奥氏体相变与断裂机制研究[J].塑性工程学报, 2009,16(1):156-159.Liu Qiang, Jiang Hai-tao, Tang Di, et al. Transformation behavior of retained austenite in TRIP steel under stress-strain[J]. Journal of Plasticity Engineering, 2009,16(1):156-159.
[8] 熊自柳,江海涛,蔡庆伍,等. 消除TRIP钢屈服平台的预拉伸实验及微观机理[J].北京科技大学学报, 2008,30(4):379-382.Xiong Zi-liu, Jiang Hai-tao,Cai Qing-wu, et al. Tension test and microstructural mechanism for eliminating the yield platform of TRIP steel[J].Journal of University of Science and Technology Beijing, 2008,30(4):379-382.
[9] 班丽丽,惠卫军,雍岐龙,等. 不同强度中碳TRIP钢的高周疲劳破坏行为[J].材料研究学报,2008,22(6):629-632.Ban Li-li, Hui Wei-jun, Yong Qi-long,et al. High cycle fatigue behavior of medium-carbon TRIP steel at different tensile strength levels[J]. Chinese Journal of Materials Research,2008,22(6):629-632.
[1] GUAN Qing-feng,ZHANG Fu-tao,PENG Tao,LYU Peng,LI Yao-jun,XU Liang,DING Zuo-jun. Hot deformation behavior of 9%Cr steel contained B and Co elements [J]. Journal of Jilin University(Engineering and Technology Edition), 2018, 48(6): 1799-1805.
[2] GUAN Qing-feng, DONG Shu-heng, ZHENG Huan-huan, LI Chen, ZHANG Cong-lin, LV-Peng. Cr surface alloying of 45# steel by high-current pulsed electron beam treatment [J]. 吉林大学学报(工学版), 2018, 48(4): 1161-1168.
[3] ZHAO Yu-guang, YANG Xue-hui, XU Xiao-feng, ZHANG Yang-yang, NING Yu-heng. Effects of Al-10Sr modifiers with different states, modification temperature and holding time on microstructure of ZL114A alloy [J]. 吉林大学学报(工学版), 2018, 48(1): 212-220.
[4] TANG Hua-guo, MA Xian-feng, ZHAO Wei, LIU Jian-wei, ZHAO Zhen-ye. Synthesis microstructure and thermal properties of high performance bulk Al [J]. 吉林大学学报(工学版), 2017, 47(5): 1542-1547.
[5] GUAN Qing-feng, ZHANG Yuan-wang, SUN Xiao, ZHANG Chao-ren, LYU Peng, ZHANG Cong-lin. Surface alloying of Al-W alloy by high current pulsed electron beam treatment [J]. 吉林大学学报(工学版), 2017, 47(4): 1171-1178.
[6] YANG Xiao-hong, HANG Wen-xian, QIN Shao-gang, LIU Yong-bing, LIU Li-ping. Microstructure and wear properties of Co-based composite coatings on H13 steel surface by laser cladding [J]. 吉林大学学报(工学版), 2017, 47(3): 891-899.
[7] GUAN Qing-feng, HUANG Wei, LI Huai-fu, GONG Xiao-hua, ZHANG Cong-lin, LYU Peng. Diffusion alloying of Cu-C induced by high current pulsed electron beam [J]. 吉林大学学报(工学版), 2016, 46(6): 1967-1973.
[8] ZHANG Xue-guang, LIU Chun-guo, ZHENG Yuan, JIANG Zhong-hai, LI Xiang-ji. Forming limit prediction of aluminum alloy based on ductile damage and shear damage [J]. 吉林大学学报(工学版), 2016, 46(5): 1558-1566.
[9] LIU Xiao-bo, ZHOU De-kun, ZHAO Yu-guang. Microstructure and mechanical property of Mg2Si/Al composites fabricated by semi-solid extrusion under different isothermal heat treatments [J]. 吉林大学学报(工学版), 2016, 46(5): 1577-1582.
[10] LI Chun-ling, FAN Ding, WANG Bin, YU Shu-rong. 5A06 aluminum alloy and galvanized steel butt welding-brazing by laser with preset filler powder [J]. 吉林大学学报(工学版), 2016, 46(2): 516-521.
[11] ZHANG Jia-tao, ZHAO Yu-guang, TAN Juan. Effect of starting microstructure on refining potency of electro-pulsing on reverse austenite grain [J]. 吉林大学学报(工学版), 2016, 46(1): 193-198.
[12] GUAN Qing-feng, LI Yan, HOU Xiu-li, YANG Sheng-zhi, WANG Xiao-tong. Modification of solid solution Mg-Gd-Y-Nd alloy irradiated by high current pulsed electron beam [J]. 吉林大学学报(工学版), 2015, 45(4): 1200-1205.
[13] MA Yun-hai, SHANG Wen-bo, FAN Xue-ying, GAO Zhi-hui, TONG Jin, YAN Zhi-feng, CHANG Zhi-yong. Preparation and degradation of porous β-tricalcium phosphate bioceramic for bone imitaion [J]. 吉林大学学报(工学版), 2015, 45(4): 1367-1374.
[14] DUAN Xing-wang,LIU Jian-sheng. Plasticity at elevated temperature and fracture character of 316LN steel [J]. 吉林大学学报(工学版), 2015, 45(2): 494-500.
[15] GAO Song, LIANG Ji-cai, CHEN Guang-yi, WEI Zhi-yong, TENG Fei. Rapid adjusting of fundamental units in process of flexible 3D stretch-bending [J]. 吉林大学学报(工学版), 2014, 44(6): 1723-1728.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!