类金刚石涂层与未涂层镍钛丝在人工唾液中耐腐蚀性能的比较

doi:10.13481/j.1671-587x.20160319

Abstract

Abstract:

Objective: To compare the corrosion resistance abilities between diamond-like carbon (DLC)coated nickel-titanium arch(NiTi) wires and uncoated NiTi wires in the artificial saliva with different pH values and fluoride(F^-)concentrations, and to provide the basis for the application of DLC in the orthodontics treatment. Methods: The DLC coated NiTi wires were prepared by radio-frequency magnetron sputtering technique. Raman spectrum was used to characterizate the NiTi wires. The DLC coated wires were taken as experiment group, and the uncoated NiTi wires were taken as control group, and the NiTi wires in two groups were exposed to four kinds of artificial saliva as four groups, pH7＋0%F^- group: pH 7+0.2% F^- group,pH7+0.5% F^- group,and pH5+0.5% F^- group.The potentiodynamic polarization (Tafel)curves of NiTi wires in two groups were measured by the classic three electrode system of electrochemical workstation,and the corrosion potential (Ecorr) and the corrosion current density (Icorr)of the NiTi wires in two groups were detected; scanning electron microscope(SEM) was used to observe the morphology of the NiTi wires in two groups before and after corrosion with artificial saliva. Results: The Raman spectra results showed the typical D peak and G peak,which indicated that the NiTi wires had been coated by DLC. The electrochemical corrosion test showed that compared with pH7+0% F^- group,the Ecorr of DLC coated NiTi wires in pH7+0.2% F^- group was decreased(P<0.05)and the Icorr was increased(P<0.05);the Ecorr of uncoated NiTi wires was decreased(P<0.05),and the Icorr was increased,but there was no significant difference(P>0.05).Compared with pH7+0.5% F^- group, the Ecorr of DLC coated NiTi wires and uncoated NiTi wires in pH5+0.5% F^-group were decreased(P<0.05)and the Icorr were increased(P<0.05). Meanwhile,in the same group of artificial saliva,the Ecorr of NiTi wires in expiment group was apparently higher than that in control group(P<0.05)and the Icorr was lower than that in control group(P<0.05). The Tafel curves of NiTi wires in two groups were moved to the left with the increasing of F^- concentration and the decreasing of pH value,which indicated that the corrosion resistance ability was decreased. Under scanning electron microscope, much pitting corrosion was observed on the surface of NiTi wires in control group than experiment group. Conclusion: The corrosion resistance ability of DLC coated NiTi wires is higher than that of uncoated NiTi wires,but the increasing of F^- concentration and the decreasing of pH value can decrease the corrosion resistance ability of NiTi wires.

Key words: diamond-like carbon, Nickel-titanium arch wires, artificial saliva, electrochemical corrosion

CLC Number:

R783.5

WU Yanran, YANG Luyi, LIU Jun, YIN Hong, MOU Yinhe, XIA Xiaoxue, TENG Rong. Comparison of corrosion resistance abilities between diamond-like carbon coated and uncoated nickel titanium wire in artificial saliva[J].Journal of Jilin University Medicine Edition, 2016, 42(03): 517-522.

References

[1] Huang SY, Huang JJ, Kang T,et al. Coating NiTi archwires with diamond-like carbon films: reducing fluoride-induced corrosion and improving frictional properties [J].J Mater Sci: Mater Med, 2013,24(10):2287-2292.

[2] Huang H, Chiu YH, Lee TH, et al. Ion release from NiTi orthodontic wires in artificial saliva with various acidities [J]. Biomaterials, 2003,24(20): 3585-3592.

[3] Li XJ, Wang JQ, Han EH, et al.Influence of fluoride and chloride on corrosion behavior of NiTi orthodontic wires [J]. Acta Biomateria, 2007,3(5):807-815.

[4] Genelhu MC, Marigo M, Alves-Oliveira LF, et al. Characterization of nickel-induced allergic contact stomatitis associated with fixed orthodontic appliances [J]. Am J Orthod Dentofacial Orthop, 2005(128): 378-381.

[5] Prashant PS, Nandan H, Gopalakrishnan M. Friction in orthodontics [J]. J Pharm Bioallied Sci, 2015, 7(Suppl 2): 334-338.

[6] Espinar E, Llamas JM, Michiardi A, et al. Reduction of Ni release and improvement of the friction behaviour of NiTi orthodontic archwires by oxidation treatments [J]. J Mater Sci Mater Med, 2011,22(5): 1119-1125.

[7] Kobayashi S, Ohgoe Y, Ozeki K, et al. Dissolution effect and cytotoxicity of diamond-like carbon coatings on orthodontic archwires [J]. J Mater Sci Mater Med, 2007,18(12): 2263-2268.

[8] Xu JL, Liu F, Wang FP, et al. Alumina coating formed on medical NiTi alloy by micro-arc oxidation [J]. Mater Lett, 2008,62(25): 4112-4114.

[9] Sun T, Lee WC, Wang M. A comparative study of apatite coating and apatite/collagen composite coating fabricated on NiTi shape memory alloy through electrochemical deposition [J]. Mater Lett, 2011,65(17): 2575-2577.

[10] Roy RK, Lee KR. Biomedical applications of diamond-like carbon coatings: a review[J]. J Biomed Mater Res B Appl Biomater, 2007,83(1):72-84.

[11] Kusy RP, Keith O, Whitley JQ, et al. Coefficient of friction characterization of surface-modified polycrystalline alumina [J]. J Am Ceram Soc,1993, 76(2):336-342.

[12] Kobayashi S, Ohgoe Y, Ozeki K, et al. Dissolution effect and cytotoxicity of diamond-like carbon coatings on orthodontic archwires [J].J Mater Sci: Mater Med, 2007,18(12):2263-2268.

[13] Bentahar Z, Barquins M, Clin M, et al. Tribological performance of DLC-coated stainless steel, TMA and Cu-NiTi [J].Int Orthodont, 2008 (6 ): 335-342.

[14] Muguruma T,Iijima M,Brantley WA,et al. Frictional and mechanical properties of diamond-like carbon-coated orthodontic brackets [J]. Eur J Orthodont, 2011,35(2):216-222.

[15] Chaturvedi TP. An overview of the corrosion aspect of dental implants (titanium and its alloys)[J]. Indian J Dent Res, 2009, 20(1):91-98.

[16] Wang Q, Zhang Y, Hao FY, et al. Comparative study of clinically used NiTi orthodontic wires[J].Int J Mod PhysB, 2010, 24 (30): 5929-5937.

[17] 马长柏,刘新强,李金华. 氟对镍钛弓丝的腐蚀性研究[J].现代口腔医学杂志, 2009, 23(6):587-590.

[18] Yokoyama K, Kaneko K, Moriyama K, et al. Hydrogen embrittlement of NiTi super elastic alloy in fluoride solution [J].J Biomed Mater ResA, 2003(65):182-187.

Comparison of corrosion resistance abilities between diamond-like carbon coated and uncoated nickel titanium wire in artificial saliva

PDF (PC)

Like

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 1

Metrics

Comments

Recommended 10