AZ31合金的平均晶粒尺寸与单道次轧制变形量之间的量化关系

doi:10.13229/j.cnki.jdxbgxb201602026

吉林大学学报(工学版) ›› 2016, Vol. 46 ›› Issue (2): 505-510.doi: 10.13229/j.cnki.jdxbgxb201602026

AZ31合金的平均晶粒尺寸与单道次轧制变形量之间的量化关系

赵世喆¹, 周宏¹, 佟国栋², 李文平¹, 关峰¹

1.吉林大学汽车材料教育部重点实验室,长春 130022;
2.中国第一汽车集团公司一汽铸造有限公司,长春 130062

收稿日期:2015-04-23 出版日期:2016-02-20 发布日期:2016-02-20
通讯作者: 周宏(1956-),男,博士生导师.研究方向:镁合金.E-mail:zhouhong@jlu.edu.cn E-mail:zszcrazy@me.com
作者简介:赵世喆(1983-),男,博士研究生.研究方向:稀土镁合金.E-mail:zszcrazy@me.com
基金资助:
国家科技支撑计划项目(2011BAE22B06-1)

Quantitative relationship between average grain size and maximum simple pass rolling deformation of Mg-3Al-1Zn

ZHAO Shi-zhe¹, ZHOU Hong¹, TONG Guo-dong², LI Wen-ping¹, GUAN Feng¹

1.Key Laboratory of Automobile Materials of Ministry of Education, Jilin University, Changchun 130022, China;
2.FAW foundry Co., Ltd., China FAW Group Corporation,Changchun 130062, China

Received:2015-04-23 Online:2016-02-20 Published:2016-02-20

摘要/Abstract

摘要： 研究了AZ31平均晶粒尺寸与单道次轧制变形量之间的关系,引入了形状因子概念,并计算了关于三者的回归方程,从数学方面分析了β相对AZ31合金变形性能的影响.通过固溶处理去除了β相,得到了AZ31平均晶粒尺寸与变形量之间的准确量化关系,为简化轧制生产提供了参考.

关键词: 材料合成与加工工艺, 轧制, AZ31合金, 回归方程, 平均晶粒尺寸, 固溶处理

Abstract: The quantitative relationship between average grain size and simple pass rolling deformation of magnesium alloy is studied. The concept of shape factor is introduced and the regression equation of them is calculated. The effect of β phase on the deformation property of AZ31 alloy is mathematically analyzed. The β phase can be deleted by homogenization treatment to obtain the accurate regression equation between grain size of AZ31 alloy and simple pass rolling deformation. This study may provide a direct reference to simplify the rolling production.

Key words: materials synthesis and processing technology, rolling, AZ31 alloy, regression equation, average grain size, homogenization treatment

中图分类号:

TG146

赵世喆, 周宏, 佟国栋, 李文平, 关峰. AZ31合金的平均晶粒尺寸与单道次轧制变形量之间的量化关系[J]. 吉林大学学报(工学版), 2016, 46(2): 505-510.

ZHAO Shi-zhe, ZHOU Hong, TONG Guo-dong, LI Wen-ping, GUAN Feng. Quantitative relationship between average grain size and maximum simple pass rolling deformation of Mg-3Al-1Zn[J]. 吉林大学学报(工学版), 2016, 46(2): 505-510.

参考文献

[1] Vespa G, Mackenzie L W F, Verma R,et al. The influence of the as-hot rolled microstructure on the elevated temperature mechanical properties of magnesium AZ31 sheet[J]. Materials Science & Engineering A, 2008, 487:243-250.
[2] Suh Byeong-Chan, Shim Myeong-Shik, Shin K S,et al. Current issues in magnesium sheet alloys: where do we go from here?[J].Scripta Materialia, 2014(84-85):1-6.
[3] Kainer K U. Magnesium Alloys and Technologies[M].Weinheim: WILEY-VCH Verlag GmbH & Co. KG aA, 2003:8-9.
[4] Chen Xing-pin, Shang Du, Xiao Rui, et al. Influence of rolling ways on microstructure and anisotropy of AZ31 alloy sheet[J]. Transactions of Nonferrous Metals Society of China, 2010,20:589-593.
[5] Chang T C, Wang J Y, Lee S. Grain refining of magnesium alloy AZ31 by rolling[J]. Journal of Materials Processing Technology, 2003,140(1-3):588-591.
[6] Liu Di, Liu Zu-yan, Wang Er-de. Effect of rolling reduction on microstructure, texture, mechanical properties and mechanical anisotropy of AZ31 magnesium alloys[J]. Materials Science and Engineering:A, 2014, 612:208-213.
[7] Barnett M R, Beer A G, Atwell D, et al. Influence of grain size on hot working stresses and microstructures in Mg-3Al-1Zn[J]. Scripta Materialia, 2004,51(1):19-24.
[8] Fan H D, Aubry S, Arsenlis A,et al. Orientation influence on grain size effects in ultrafine-grained magnesium[J]. Scripta Materialia, 2015, 97:25-28.
[9] Yu Kun, Rui Shou-tai, Song Jue-min, et al. Effects of grain refinement on mechanical properties and microsturctures of AZ31 alloy[J]. Transactions of Nonferrous Metals Society of China, 2008,18:39-43.
[10] 李文平,周宏,赵世喆,等.镝对AZ31合金β相形状,固溶处理时间及单道次最大轧制率的影响[J].吉林大学学报:工学版,2009,39(4):941-944.
Li Wen-ping, Zhou Hong, Zhao Shi-zhe, et al. Effect of dysprosium on shape of β phase, homogenization treatment time and maximum reduction per rolling pass of AZ31 alloy[J]. Journal of Jilin University (Engineering and Technology Edition), 2009,39(4):941-944.

相关文章 15

[1]	姜秋月,杨海峰,檀财旺. 22MnB5超高强钢焊接接头强化性能[J]. 吉林大学学报(工学版), 2018, 48(6): 1806-1810.
[2]	胡志清, 颜庭旭, 李洪杰, 吕振华, 廖伟, 刘庚. 深冷处理对铝合金薄板冲剪成形性能的影响[J]. 吉林大学学报(工学版), 2018, 48(5): 1524-1530.
[3]	邱小明, 王银雪, 姚汉伟, 房雪晴, 邢飞. 基于灰色关联的DP1180/DP590异质点焊接头工艺参数优化[J]. 吉林大学学报(工学版), 2018, 48(4): 1147-1152.
[4]	陈俊甫, 管志平, 杨昌海, 牛晓玲, 姜振涛, 宋玉泉. 金属棒试样拉伸和扭转试验应变范围和力学特性对比[J]. 吉林大学学报(工学版), 2018, 48(4): 1153-1160.
[5]	梁晓波, 蔡中义, 高鹏飞. 夹芯复合板柱面成形的数值模拟及试验[J]. 吉林大学学报(工学版), 2018, 48(3): 828-834.
[6]	刘子武, 李剑峰. 叶片材料FV520B再制造熔覆层冲蚀损伤行为及评价[J]. 吉林大学学报(工学版), 2018, 48(3): 835-844.
[7]	刘纯国, 刘伟东, 邓玉山. 多点冲头主动加载路径对薄板拉形的影响[J]. 吉林大学学报(工学版), 2018, 48(1): 221-228.
[8]	张志强, 刘从豪, 何东野, 李湘吉, 李纪萱. 基于性能梯度分布的硼钢热冲压工艺对形状精度的影响[J]. 吉林大学学报(工学版), 2017, 47(6): 1829-1833.
[9]	吕萌萌, 谷诤巍, 徐虹, 李欣. 超高强度防撞梁热冲压成形工艺优化[J]. 吉林大学学报(工学版), 2017, 47(6): 1834-1841.
[10]	王辉, 周杰, 熊煜, 陶亚平, 向荣. 基于逆向工程的复杂曲面冲压件回弹补偿[J]. 吉林大学学报(工学版), 2017, 47(6): 1842-1847.
[11]	王春生, 邹丽, 杨鑫华. 基于邻域粗糙集的铝合金焊接接头疲劳寿命影响因素分析[J]. 吉林大学学报(工学版), 2017, 47(6): 1848-1853.
[12]	邢海燕, 葛桦, 李思岐, 杨文光, 孙晓军. 基于模糊隶属度最大似然估计的焊缝隐性缺陷磁记忆信号识别[J]. 吉林大学学报(工学版), 2017, 47(6): 1854-1860.
[13]	谷晓燕, 刘亚俊, 孙大千, 徐锋, 孟令山, 高帅. S355钢/6005A铝合金瞬间液相扩散连接接头组织与性能[J]. 吉林大学学报(工学版), 2017, 47(5): 1534-1541.
[14]	谷诤巍, 张文学, 吕萌萌, 王伟, 徐虹, 李欣. 宽翼边U型截面不锈钢型材拉弯成形缺陷控制[J]. 吉林大学学报(工学版), 2017, 47(4): 1165-1170.
[15]	寇淑清, 宋玮峰, 石舟. 36MnVS4连杆裂解加工模拟及缺陷分析[J]. 吉林大学学报(工学版), 2017, 47(3): 861-868.

Metrics

Viewed

Full text

Abstract

Cited

Shared

Discussed

AZ31合金的平均晶粒尺寸与单道次轧制变形量之间的量化关系

Quantitative relationship between average grain size and maximum simple pass rolling deformation of Mg-3Al-1Zn

RICH HTML

PDF (PC)

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

本文评价

推荐阅读 10