Journal of Jilin University(Engineering and Technology Edition) ›› 2019, Vol. 49 ›› Issue (4): 1162-1168.doi: 10.13229/j.cnki.jdxbgxb20171296

Previous Articles    

Effect of carbonation on nitrite ion distribution in cement paste

Xiao⁃zhen LI(),Jun⁃zhe LIU(),Yan⁃hua DAI,Zhi⁃min HE,Ming⁃fang BA,Yu⁃shun LI   

  1. College of Architectural, Civil Engineering and Environment, Ningbo University, Ningbo 315211, China
  • Received:2017-12-31 Online:2019-07-01 Published:2019-07-16
  • Contact: Jun?zhe LIU E-mail:lixiaozhen01@126.com;junzheliu@163.com

RICH HTML

 3   

PDF (PC)

102

Abstract:

The influence of carbonization on the distribution of nitrite ions in hardened cement paste is verified by electron probe microanalysis (EPMA) and X-ray diffraction (XRD), and the migration and adsorption of free nitrite ions in cement paste is clarified, which is important to accurately evaluates the corrosion-resistant effect of nitrite ion on reinforced concrete. The results reveal that a new hydrated crystallization phase NO2?AFm is produced after the hydration of nitrite-containing cement paste and is evenly distributed. During the carbonation process, NO2?AFm re-decomposes and generates nitrite ions, diffusing to non-carbonized area. This results in a decrease of NO2?content in carbonized area and an increase in non-carbonized area. Nevertheless, due to the decomposition of C?S?H gel during the carbonization process, the free nitrite ions adsorbed on its surface are re?transformed into free nitrite ion, increasing the content of free nitrite in the carbonization area. Meanwhile, the migration of silicon from carbonized area into non?carbonized area, contributes to a higher amorphous content of C?S?H gel in non-carbonized area, which increases the solidified effect of nitrite ion, and eventually leads to a higher nitrite ion content in carbonized area than that in non-carbonized area.

Key words: road engineering, cement paste, carbonation, nitrite ion, electron probe microanalysis(EPMA), NO2?AFm

CLC Number: 

  • TQ172

Fig.1

"

Fig.2

Distribution of free nitrite ion after carbonation"

Fig.3

XRD patterns of cement paste containing nitrite"

Fig.4

Distribution of Si elements after carbonation"

Fig.5

XRD patterns of cement paste containing nitrite after carbonation"

1 Marques P F , Chastre C , Nunes A . Carbonation service life modelling of RC structures for concrete with Portland and blended cements[J]. Cement and Concrete Composites, 2013, 37(6):171⁃184.
2 Kwon S J , Song H W . Analysis of carbonation behavior in concrete using neural network algorithm and carbonation modeling[J]. Cement and Concrete Research, 2010, 40(1): 119⁃127.
3 Liu Jun⁃zhe , Ba Ming⁃fang , Du Yin⁃gang , et al . Effects of chloride ions on carbonation rate of hardened cement paste by X⁃ray CT technic[J]. Construction and Building Materials, 2016, 122(7): 619⁃627.
4 Li Qin⁃fei , Ge Yong , Yang Wen⁃cui . Effect of sodium sulfate and sodium nitrite on air⁃void system in airentrained concrete[J]. Magazine of Concrete Research, 2016, 68(23): 1200⁃1209.
5 Fayala I , Dhouibi L , Nóvoa X R , et al . Effect of inhibitors on the corrosion of galvanized steel and on mortar properties[J]. Cement Concrete Comp, 2013, 35(1): 181⁃189.
6 Goulart C M , Esteves-Souza A , Martinez⁃Huitle C A , et al . Experimental and theoretical evaluation of semicarbazones and thiosemicarbazones as organic corrosion inhibitors[J]. Corrosion Science, 2013, 67:281⁃291.
7 Rakanta E , Zafeiropoulou T , Batis G . Corrosion protection of steel with DMEA⁃based organic inhibitor[J]. Construction and Building Materials, 2013, 44:507⁃513.
8 Verbruggen H , Terryn H , De Graeve I . Inhibitor evaluation in different simulated concrete pore solution for the protection of steel rebar[J]. Construction and Building Materials, 2016, 124: 887⁃896.
9 Mu G N , Li X H , Qu Q . Molybdate and tungstate as corrosion inhibitors for cold rolling steel in hydrochloric acid solution[J]. Corrosion Science, 2006, 48(2): 445⁃459.
10 Sanchez M , Alonso M C . Electrochemical chloride removal in reinforced concrete structures: improvement of effectiveness by simultaneous migration of calcium nitrite[J]. Construction and Building Materials, 2011, 25(2): 873⁃878.
11 Wong H S , Zhao Y X , Karimi A R , et al . On the penetration of corrosion products from reinforcing steel into concrete due to chloride⁃induced corrosion[J]. Corrosion Science, 2010, 52(7): 2469⁃2480.
12 Álvarez⁃Bustamante R , Negrón⁃Silva G , Abreu⁃Quijano M . Electrochemical study of 2⁃merca⁃ ptoimidazole as a novel corrosion inhibitor for steels[J]. Electrochimica Acta, 2009, 54(23): 5393⁃5399.
13 Valcarce M B , Vázquez M . Carbon steel passivity examined in solutions with a low degree of carbonation: the effect of chloride and nitrite ions[J]. Materials Chemistry and Physics, 2009, 115(1): 313⁃321.
14 El Haleem S M A , El Wanees S A , El Aal E E A , et al . Environmental factors affecting the corrosion behavior of reinforcing steel. IV. variation in the pitting corrosion current in relation to the concentration of the aggressive and the inhibitive anions[J]. Corrosion Science, 2010, 52(5): 1675⁃1683.
15 Yohai L , Schreiner W , Valcarce M B , et al . Inhibiting steel corrosion in simulated concrete with low phosphate to chloride ratios[J]. Journal of the Electrochemical Society, 2016, 163(13): 729⁃737.
16 Okeniyi J O , Omotosho O A , Ajayi O O . Effect of potassium⁃chromate and sodium⁃nitrite on concrete steel⁃rebar degradation in sulphate and saline media[J]. Construction and Building Materials, 2014, 50: 448⁃456.
17 柳俊哲, 袁伟静, 贺智敏, 等 . 碳化对混凝土碱骨料反应的影响[J]. 吉林大学学报: 工学版, 2015, 45(3): 783⁃787.
Liu Jun⁃zhe , Yuan Wei⁃jing , He Zhi⁃min , et al . Influence of carbonation on alkali⁃aggregate reaction in concrete[J]. Journal of Jilin University(Engineering and Technology Edition), 2015, 45(3): 783⁃787.
18 Al⁃Mehthel M , Al⁃Dulaijan S , Al⁃Idi S H , et al . Performance of generic and proprietary corrosion inhibitors in chloride⁃contaminated silica fume cement concrete[J]. Construction and Building Materials, 2009, 23(5): 1768⁃1774.
19 Tommaselli M A G , Mariano N A , Kuri S E . Effectiveness of corrosion inhibitors in saturated calcium hydroxide solutions acidified by acid rain components[J]. Construction and Building Materials, 2009, 23(1): 328⁃333.
20 Lee H , Ryu H , Park W , et al . Comparative study on corrosion protection of reinforcing steel by using amino alcohol and lithium nitrite inhibitors[J]. Materials, 2015, 8(1): 251⁃269.
21 Han Jian⁃de , Pan Gang⁃hua , Sun Wei . Investigation on carbonation induced meso⁃defects changes of cement mortar using 3D X⁃Ray computed tomography[J]. Journal of the Chinese Ceramic Society, 2011, 399(10):75⁃79.
22 Lu S , Landis E N , Keane D T . X⁃ray microtomographic studies of pore structure and permeability in portland cement concrete[J]. Materials and Structures, 2006, 39(6): 611⁃620.
23 Rougelot T , Burlion N , Bernard D D , et al . About microcracking due to leaching in cementitious composites: X⁃ray microtomography description and numerical approach[J]. Cement and Concrete Research, 2010, 40(2): 271⁃283.
24 Cao Yan⁃hui , Dong Shi⁃gang . Multifunctional inhibition based on layered double hydroxides to comprehensively control corrosion of carbon steel in concrete[J]. Corrosion Science, 2017, 126(9):166⁃179.
[1] Tian⁃lai YU,Hai⁃sheng LI,Wei HUANG,Si⁃jia WANG. Shear strengthening of reinforced concrete beam with prestressed steel wire ropes [J]. Journal of Jilin University(Engineering and Technology Edition), 2019, 49(4): 1134-1143.
[2] Xiao⁃ming HUANG,Qing⁃qing CAO,Xiu⁃yu LIU,Jia⁃ying CHEN,Xing⁃lin ZHOU. Simulation of vehicle braking performance on rainy daysbased on pavement surface fractal friction theory [J]. Journal of Jilin University(Engineering and Technology Edition), 2019, 49(3): 757-765.
[3] Jing WANG,Xiang LYU,Xiao⁃long QU,Chun⁃ling ZHONG,Yun⁃long ZHANG. Analysis of relationship between subgrade soil shear strength and chemical and minerals component [J]. Journal of Jilin University(Engineering and Technology Edition), 2019, 49(3): 766-772.
[4] LI Yi,LIU Li-ping,SUN Li-jun. Prediction model on rutting equivalent temperature for asphalt pavement at different depth [J]. Journal of Jilin University(Engineering and Technology Edition), 2018, 48(6): 1703-1711.
[5] ZANG Guo-shuai, SUN Li-jun. Method based on inertial point for setting depth to rigid layer [J]. 吉林大学学报(工学版), 2018, 48(4): 1037-1044.
[6] NIAN Teng-fei, LI Ping, LIN Mei. Micro-morphology and gray entropy analysis of asphalt characteristics functional groups and rheological parameters under freeze-thaw cycles [J]. 吉林大学学报(工学版), 2018, 48(4): 1045-1054.
[7] GONG Ya-feng, SHEN Yang-fan, TAN Guo-jin, HAN Chun-peng, HE Yu-long. Unconfined compressive strength of fiber soil with different porosity [J]. 吉林大学学报(工学版), 2018, 48(3): 712-719.
[8] CHENG Yong-chun, BI Hai-peng, MA Gui-rong, GONG Ya-feng, TIAN Zhen-hong, LYU Ze-hua, XU Zhi-shu. Pavement performance of nano materials-basalt fiber compound modified asphalt binder [J]. 吉林大学学报(工学版), 2018, 48(2): 460-465.
[9] JI Wen-yu, LI Wang-wang, GUO Min-long, WANG Jue. Experimentation and calculation methods of prestressed RPC-NC composite beam deflection [J]. 吉林大学学报(工学版), 2018, 48(1): 129-136.
[10] ZHANG Yang-peng, WEI Hai-bin, JIA Jiang-kun, CHEN Zhao. Numerical evaluation on application of roadbed with composite cold resistance layer inseasonal frozen area [J]. 吉林大学学报(工学版), 2018, 48(1): 121-126.
[11] MA Ye, NI Ying-sheng, XU Dong, DIAO Bo. External prestressed strengthening based on analysis of spatial grid model [J]. 吉林大学学报(工学版), 2018, 48(1): 137-147.
[12] LUO Rong, ZENG Zhe, ZHANG De-run, FENG Guang-le, DONG Hua-jun. Moisture stability evaluation of asphalt mixture based on film pressure model of Wilhelmy plate method [J]. 吉林大学学报(工学版), 2017, 47(6): 1753-1759.
[13] NI Ying-sheng, MA Ye, XU Dong, LI Jin-kai. Space mesh analysis method for shear lag effect of cable-stayed bridge with corrugated steel webs [J]. 吉林大学学报(工学版), 2017, 47(5): 1453-1464.
[14] ZHENG Chuan-feng, MA Zhuang, GUO Xue-dong, ZHANG Ting, LYU Dan, Qin Yong. Coupling effect of the macro and micro characteristics of mineral powder on the low-temperature performance of asphalt mortar [J]. 吉林大学学报(工学版), 2017, 47(5): 1465-1471.
[15] YU Tian-lai, ZHENG Bin-shuang, LI Hai-sheng, TANG Ze-rui, ZHAO Yun-peng. Analyses of defects and causes of steel-plastic compound reinforced retaining wall [J]. 吉林大学学报(工学版), 2017, 47(4): 1082-1093.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
Copyright © Journal of Jilin University(Engineering and Technology Edition), All Rights Reserved.
Tel: +86-431-85095297　Fax: +86-431-85094074　E-mail: xbgxb@jlu.edu.cn
Powered by Beijing Magtech Co. Ltd