5A06 aluminum alloy and galvanized steel butt welding-brazing by laser with preset filler powder

LI Chun-ling, FAN Ding, WANG Bin, YU Shu-rong   

  1. State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals, Lanzhou University of Technology, Lanzhou 730050, China
  • Received:2014-04-09 Online:2016-02-20 Published:2016-02-20

RICH HTML

2   

PDF (PC)

346

Abstract: Laser welding-brazing of 5A06 aluminum alloy and galvanized steel sheet with filler powder was carried out. The obtained butt joint exhibited dual characteristics. The interfacial properties and microstructure of the joints examined using Scanning Electron Microscopy (SEM), Energy Dispersive Spectrometer (EDS) and X-ray Diffraction (XRD), and the tensile strength was measured. Results show that a non-uniform intermetallic compound (IMC) with serrated shape is formed at the interfacial layer, which is composed of Fe2Al5 and FeAl3. The thickness of the IMC layer varies from 2.5 ~ 7 μm, and it increases with the laser power. At the top surface of the galvanized steel the IMC layer reaches the thickest. Using this laser welding-brazing method with special filler powder, the IMC thickness can be controlled to less than 10 μm, and butt joints with certain tensile strength can be obtained under appropriate welding parameters.

Key words: metallic materials, aluminum alloy and steel, laser welding-brazing, intermetallic compounds, mechanical property

CLC Number: 

  • TG456
[1] Sierra G, Peyre P, Deschaux-Beaume F, et al. Steel to aluminum key-hole laser welding[J]. Materials Science and Engineering A, 2007, 447(1/2): 197-208.
[2] 赵旭东, 肖荣诗. 铝-钢异种金属无钎剂激光填粉熔钎焊接[J]. 中国激光, 2012, 39(4):0403004.
Zhao Xu-dong, Xiao Rong-shi. Fluxless joining between aluminum alloy and galvanized steel by fiber laser fusion welding-brazing with filler power[J]. Chinese Journal of Lasers, 2012, 39(4):0403004.
[3] Zhang M J, Chen G Y, Zhang Y, et al. Research on microstructure and mechanical properties of laser keyhole welding-brazing of automotive galvanized steel to aluminum alloy[J]. Materials and Design, 2013, 45: 24-30.
[4] Mei S W, Gao M, Yan J, et al. Interface properties and thermodynamic analysis of laser-arc hybrid welded Al/steel joint[J]. Science and Technology of Welding and Joining, 2013, 18(4): 293-300.
[5] 秦国梁, 苏玉虎, 王术军. 铝合金/镀锌钢板脉冲MIG电弧熔-钎焊接头组织与性能[J]. 金属学报, 2012, 48(8): 1018-1024.
Qin Guo-liang, Su Yu-hu, Wang Shu-jun. Microstructures and properties of pulsed MIG arc brazed-fusion welded joint of Al alloy and galvanized steel[J]. Acta Metallurgica Sinica, 2012, 48(8): 1018-1024.
[6] Rathod M, Kutsuna M. Use of pulsed CO 2 laser in laser roll bonding of A5052 aluminum alloy and low carbon steel[J]. Welding in the Wor1d, 2006, 50(7/8): 28-36.
[7] Dharmendra C, Rao K P, Wilden J, et al. Study on laser welding-brazing of zinc coated steel to aluminum alloy with a zinc based filler[J]. Materials Science and Engineering A, 2011, 528(3): 1497-1503.
[8] 樊丁, 蒋锴, 余淑荣, 等. 5052铝合金/镀锌钢涂粉CO 2 激光熔钎焊工艺特性[J]. 焊接学报, 2014, 35(1): 1-4.
Fan Ding, Jiang Kai, Yu Shu-rong, et al. Characteristic of fusion-brazed joint between 5052 aluminum alloy and zinc-coated steel by CO 2 laser[J]. Transactions of the China Welding Institution, 2014, 35(1): 1-4.
[9] 陈树海, 马柯, 黄继华. 钢/铝异种金属双熔池TIG熔钎焊接头的显微组织与力学性能[J]. 中国有色金属学报, 2011, 21(12): 3076-3081.
Chen Shu-hai , Ma Ke , Huang Ji-hua. Microstructure and mechanical property of joint by TIG welding- brazing with dual weld pools for steel/aluminum dissimilar metals[J]. The Chinese Journal of Nonferrous Metals, 2011, 21(12): 3076-3081.
[10] Agudo L, Eyidi D, Schmaranzer C H, et al. Intermetallic FexAly-phases in a steel/Al-alloy fusion weld[J]. Journal of Materials Science, 2007, 42(12): 4205-4214.
[11] 黄健康, 何翠翠, 石玗, 等. 铝/钢异种金属焊接接头界面Al-Fe金属间化合物生成及其热力学分析[J]. 吉林大学学报:工学版, 2014, 44(4): 1037-1041.
Huang Jian-kang, He Cui-cui, Shi Yu, et al. Thermodynamic analysis of Al-Fe intermetallic compounds formed by dissimilar joining of aluminum and galvanized steel[J]. Journal of Jilin University(Engineering and Technology Edition), 2014, 44(4): 1037-1041.
[12] Heumann T, Dittrich N A. Structure character of the Fe 2 Al 5 intermetallics compound in hot dip aluminizing process[J]. Zeitschrift fur Metallkunde, 1959, 50: 617-623.
[13] Lin S B, Song J L, Ma G C, et al. Dissimilar metals TIG welding-brazing of aluminum alloy to galvanized steel[J]. Frontiers of Materials Science in China, 2009, 3(1): 78-83.
[1] ZHUNG Wei-min, ZHAO Wen-zeng, XIE Dong-xuan, LI Bing. Joint performance analysis on connection of ultrahigh-strength steel and aluminum alloy with hot riveting [J]. 吉林大学学报(工学版), 2018, 48(4): 1016-1022.
[2] ZHAO Yu-guang, YANG Xue-hui, XU Xiao-feng, ZHANG Yang-yang, NING Yu-heng. Effects of Al-10Sr modifiers with different states, modification temperature and holding time on microstructure of ZL114A alloy [J]. 吉林大学学报(工学版), 2018, 48(1): 212-220.
[3] GU Xiao-yan, LIU Ya-jun, SUN Da-qian, XU Feng, MENG Ling-shan, GAO Shuai. Microstructures and mechanical properties of transient liquid phase diffusion bonded S355 steel/6005A aluminum alloy joint [J]. 吉林大学学报(工学版), 2017, 47(5): 1534-1541.
[4] TANG Hua-guo, MA Xian-feng, ZHAO Wei, LIU Jian-wei, ZHAO Zhen-ye. Synthesis microstructure and thermal properties of high performance bulk Al [J]. 吉林大学学报(工学版), 2017, 47(5): 1542-1547.
[5] LIU Xiao-bo, ZHOU De-kun, ZHAO Yu-guang. Microstructure and mechanical property of Mg2Si/Al composites fabricated by semi-solid extrusion under different isothermal heat treatments [J]. 吉林大学学报(工学版), 2016, 46(5): 1577-1582.
[6] ZHANG Jia-tao, ZHAO Yu-guang, TAN Juan. Effect of starting microstructure on refining potency of electro-pulsing on reverse austenite grain [J]. 吉林大学学报(工学版), 2016, 46(1): 193-198.
[7] GUAN Qing-feng, LI Yan, HOU Xiu-li, YANG Sheng-zhi, WANG Xiao-tong. Modification of solid solution Mg-Gd-Y-Nd alloy irradiated by high current pulsed electron beam [J]. 吉林大学学报(工学版), 2015, 45(4): 1200-1205.
[8] MA Yun-hai, SHANG Wen-bo, FAN Xue-ying, GAO Zhi-hui, TONG Jin, YAN Zhi-feng, CHANG Zhi-yong. Preparation and degradation of porous β-tricalcium phosphate bioceramic for bone imitaion [J]. 吉林大学学报(工学版), 2015, 45(4): 1367-1374.
[9] GAO Song, LIANG Ji-cai, CHEN Guang-yi, WEI Zhi-yong, TENG Fei. Rapid adjusting of fundamental units in process of flexible 3D stretch-bending [J]. 吉林大学学报(工学版), 2014, 44(6): 1723-1728.
[10] HUANG Jian-kang, HE Cui-cui, SHI Yu, FAN Ding. Thermodynamic analysis of Al-Fe intermetallic compounds formed by dissimilar joining of aluminum and galvanized steel [J]. 吉林大学学报(工学版), 2014, 44(4): 1037-1041.
[11] LI Xin,WANG Gang,LU Guan-han,GU Zheng-wei,XU Hong. Weldability of 22MnB5 after hot stamping by TIG welding processes [J]. 吉林大学学报(工学版), 2014, 44(3): 708-711.
[12] GUAN Qing-feng,JI Le,CAI Jie,YANG Sheng-zhi,LIU Shi-chao,ZHANG Zai-qiang,HOU Xiu-li. Surface microstructure and properties of 3Cr13 martensitic stainless steel after high current pulsed electron beam bombardment [J]. 吉林大学学报(工学版), 2014, 44(3): 712-717.
[13] CHANG Ying, LI Ye, YING Liang, LU Jin-dong, TANG Xing-hui, GUO Wei. Effect of oxidation behavior on heat transfer dynamics performance of hot stamping steel [J]. 吉林大学学报(工学版), 2013, 43(06): 1551-1557.
[14] WANG Yun, LIU Cai, MA Li-dong, WANG Yu-feng, HUANG Qing-xue. Analysis of interval between guides during two-roll straightening process [J]. 吉林大学学报(工学版), 2013, 43(03): 677-681.
[15] WANG Su-fen, PENG Yan, LI Zhi-jie, XIAO Li-zi. Cold rolling mechanical characteristics of low carbon base plate produced by compact strip production [J]. 吉林大学学报(工学版), 2012, 42(增刊1): 221-224.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
Copyright © Journal of Jilin University(Engineering and Technology Edition), All Rights Reserved.
Tel: +86-431-85095297　Fax: +86-431-85094074　E-mail: xbgxb@jlu.edu.cn
Powered by Beijing Magtech Co. Ltd