Journal of Jilin University(Engineering and Technology Edition) ›› 2020, Vol. 50 ›› Issue (2): 648-653.doi: 10.13229/j.cnki.jdxbgxb20190006

Previous Articles    

Effect of admixture on properties of GRC under hydrothermal curing conditions

Juan HE1(),Cong-mi CHENG1(),Yi-nan YANG1,Ya-fang ZHANG1,Ming-feng ZHONG2   

  1. 1.School of Civil Engineering, Guangzhou University, Guangzhou 510006, China
    2.School of Materials Science & Engineering, South China University of Technology, Guangzhou 510640, China
  • Received:2019-01-04 Online:2020-03-01 Published:2020-03-08
  • Contact: Cong-mi CHENG E-mail:10319919@qq.com;congmi2008@sina.com

RICH HTML

 2   

PDF (PC)

145

Abstract:

The corrosion of glass fiber and time-dependent change of mechanical properties of glass fiber reinforced Portland cement (GRC) with or without admixture were studied by accelerated aging method with 80 ℃ hydrothermal curing. The results show that the time-dependent change of GRC mechanical properties is caused by the combined effect of cement mortar strength growth and glass fiber corrosion damage. With the extension of curing time, on the one hand, the strength of cement mortar with fly ash keeps increasing; on the other hand, fly ash inhibits the corrosion of glass fiber. As a result, the bending strength of GRC with fly ash keeps rising despite the corrosion of glass fiber. Accelerated aging test showed that the inhibition effect of fly ash on glass fiber corrosion is better than slag. It exhibited a brittle behaviour with slight corrosion of glass fiber. Hydrating phases within and around glass fibers will lead to the loss of toughening effect. So, it is more effective to evaluate degradation of GRC by the change of GRC toughness than by the change of strength.

Key words: building materials, hydrothermal curing, glass fiber reinforced cement, mineral admixture, corrosion, toughness, fly ash

CLC Number: 

  • TU528.581

Table 1

Mix proportion of GRC and reference mortar"

样品编号配合比/(kg·m-3)
水泥粉煤灰矿渣砂玻璃纤维水
SF11 0000094060360
SF2600400094060360
SF3600040094060360
S11 000001 0000360
S260040001 0000360
S360004001 0000360

Fig.1

Relationship between flexural strength and hydrothermal curing time of GRC and reference mortar"

Fig.2

Micromorphology of glass fiber in GRC without admixture at different hydrothermal curing ages"

Fig.3

Micromorphology of glass fiber in GRC with fly ash at different hydrothermal curing ages"

Fig.4

Micromorphology of glass fiber in GRC with slag at different hydrothermal curing ages"

Fig.5

Load-deflection curves of GRC under different curing conditions"

1 Dey V, Mobasher B. Quantitative characterization of accelerated aging in cement composites using flexural inverse analysis[J]. Cement & Concrete Composites, 2018, 89(5): 181-191.
2 Eiras J N, Kundu T, Bonilla M, et al. Nondestructive monitoring of ageing of alkali resistant glass fiber reinforced cement(GRC)[J]. Journal of Nondestructive Evaluation, 2013, 32(3): 300-314.
3 Alejandro E, Laura S P, Vicente S G. An alternative methodology to predict aging effects on the mechanical properties of glass fiber reinforced cements(GRC)[J]. Construction and Building Materials, 2012, 27(1) :425-431.
4 Aindow A J, Oakley D R, Proctor B A. Comparison of the weathering behaviour of GRC with predictions made from accelerated ageing tests[J]. Cement & Concrete Research, 1984, 14(2): 271-274.
5 Litherland K L, Oakley D R, Proctor B A. The use of accelerated ageing procedures to predict the long term strength of GRC composites[J]. Cement & Concrete Research, 1981, 11(3): 455-466.
6 陈尚, 葛敦世. 83-10耐碱玻璃纤维在普硅水泥中长期强度的预测[J]. 玻璃纤维, 1987(3): 6-9.
Chen Shang, Ge Dun-shi. 83-10 alkali resistant glass fiber in the prediction of long-term strength of pervasive silicon cement[J]. Glass Fiber, 1987(3): 4-7.
7 Qin X, Li X, Cai X. The applicability of alkaline-resistant glass fiber in cement mortar of road pavement: corrosion mechanism and performance analysis[J]. International Journal of Pavement Research & Technology, 2017, 10(6): 536-544.
8 崔艳玲. GRC的耐久性及其机理研究[D]. 北京: 中国建筑材料科学研究总院, 2007.
Cui Yan-ling. Studies on durability of GRC and it’s mechanism[D]. Beijing: China Building Material Academy, 2007.
9 Peled A, Jones J, Shah S P. Effect of matrix modification on durability of glass fiber reinforced cement composites[J]. Materials & Structures, 2005, 38(2): 163-171.
10 Marikunte S, Aldea C, Shah S P. Durability of glass fiber reinforced cement composites: effect of silica fume and metakaolin[J]. Advanced Cement Based Materials, 1997, 5(3/4): 100-108.
11 Purnell P, Short N R, Page C L, et al. Accelerated ageing characteristics of glass-fibre reinforced cement made with new cementitious matrices[J]. Composites Part A: Applied Science & Manufacturing, 1999, 30(9): 1073-1080.
12 Yurdakul A, Dolekcekic E, Gunkaya G, et al. The usage of newly developed glass fibre in cement structure and their characterization[J]. Construction & Building Materials, 2018, 170(5): 13-19.
13 祖群, 赵谦. 高性能玻璃纤维[M]. 北京: 国防工业出版社, 2017: 64-65.
14 梁宁慧, 缪庆旭, 刘新荣, 等. 聚丙烯纤维增强混凝土断裂韧度及软化本构曲线确定[J]. 吉林大学学报: 工学版, 2019, 49(4): 1144-1151.
Liang Ning-hui, Miao Qing-xu, Liu Xin-rong, et al. Determination of fracture toughness and softening traction-separation law of polypropylene fiber reinforced concrete[J]. Journal of Jilin University (Engineering and Technology Edition), 2019, 49(4): 1144-1151.
15 孙绪杰, 潘景龙, 郑文忠. 玻璃纤维增强聚合物混凝土小型空心砌块复合墙片的抗震性能[J]. 吉林大学学报: 工学版, 2008, 38(5): 1054-1059.
Sun Xu-jie, Pan Jing-long, Zheng Wen-zhong. Anti-seismic behavior of composite GFRP-concrete small hollow block wall[J]. Journal of Jilin University (Engineering and Technology Edition), 2008, 38(5): 1054-1059.
16 Orlowsky J, Raupach M, Cuypers H, et al. Durability modeling of glass fibre reinforcement in cementitious environment[J]. Materials & Structures, 2005, 38(2): 155-162.
17 葛敦世. 玻璃纤维碱侵蚀机理和耐碱性的探讨[J]. 玻璃纤维, 2007(1): 1-9, 14.
Ge Dun-shi. Discussion on alkali erosion mechanism and alkali resistance of glass fibers[J]. Glass Fiber, 2007(1): 1-9, 14.
18 Song M, Purnell P, Richardson I. Microstructure of interface between fibre and matrix in 10-year aged GRC modified by calcium sulfoaluminate cement[J]. Cement & Concrete Research, 2015, 76: 20-26.
[1] Jie YUAN,Xin CHEN,Hong-lin HE,Bo YANG,Xiao-jun ZHU. Repair and rejuvenation of cracked concrete by microbiologically⁃induced calcite⁃precipitation [J]. Journal of Jilin University(Engineering and Technology Edition), 2020, 50(2): 641-647.
[2] Peng-hui WANG,Hong-xia QIAO,Qiong FENG,Hui CAO,Shao-yong WEN. Durability model of magnesium oxychloride-coated reinforced concrete under the two coupling factors [J]. Journal of Jilin University(Engineering and Technology Edition), 2020, 50(1): 191-201.
[3] Qing-feng GUAN,Xin-wen YAO,Yang YANG,Ling-yan ZHANG,Di LIU,Chen LI,Peng LYU. Preparation and property of Cr alloying layer on TC4 after surface alloying induced by high current pulsed electron beam [J]. Journal of Jilin University(Engineering and Technology Edition), 2019, 49(6): 2002-2009.
[4] Jin⁃zhong LU,Wan⁃ting ZHOU,Sheng⁃yang ZHANG,Yi⁃kai SHAO,Chang⁃yu WANG,Kai⁃yu LUO. Effect of coverage layer on corrosion resistance of 6061⁃T6 aluminum alloy subjected to laser shock peening [J]. Journal of Jilin University(Engineering and Technology Edition), 2019, 49(3): 842-849.
[5] Kai⁃yu LUO,Yue⁃hua XING,Qing⁃feng CHAI,Shi⁃kai WU,Ye⁃fang YIN,Jin⁃zhong LU. Effects of laser shock peening on corrosion fatigue behaviour of 2Cr13 stainless steel [J]. Journal of Jilin University(Engineering and Technology Edition), 2019, 49(3): 850-858.
[6] GUAN Qing-feng, DONG Shu-heng, ZHENG Huan-huan, LI Chen, ZHANG Cong-lin, LV-Peng. Cr surface alloying of 45# steel by high-current pulsed electron beam treatment [J]. 吉林大学学报(工学版), 2018, 48(4): 1161-1168.
[7] GUAN Qing-feng, ZHANG Yuan-wang, SUN Xiao, ZHANG Chao-ren, LYU Peng, ZHANG Cong-lin. Surface alloying of Al-W alloy by high current pulsed electron beam treatment [J]. 吉林大学学报(工学版), 2017, 47(4): 1171-1178.
[8] YANG Yue, ZHOU Lei-lei. Effect of micro-arc oxidation treatment on corrosion resistance of aluminum friction stir welding welds [J]. 吉林大学学报(工学版), 2016, 46(2): 511-515.
[9] GAO Xiao-jian, SUN Bo-chao, YE Huan, WANG Zi-long. Influence of mineral admixtures on the rheological behavior of self-compacting concrete [J]. 吉林大学学报(工学版), 2016, 46(2): 439-444.
[10] GUAN Qing-feng, LI Yan, HOU Xiu-li, YANG Sheng-zhi, WANG Xiao-tong. Modification of solid solution Mg-Gd-Y-Nd alloy irradiated by high current pulsed electron beam [J]. 吉林大学学报(工学版), 2015, 45(4): 1200-1205.
[11] SU Xiao-ping,WANG Qing. Corrosion damage of concrete under multi-salt soaking, freezing-thawing and dry-wet cycles [J]. 吉林大学学报(工学版), 2015, 45(1): 112-120.
[12] GUAN Qing-feng,JI Le,CAI Jie,YANG Sheng-zhi,LIU Shi-chao,ZHANG Zai-qiang,HOU Xiu-li. Surface microstructure and properties of 3Cr13 martensitic stainless steel after high current pulsed electron beam bombardment [J]. 吉林大学学报(工学版), 2014, 44(3): 712-717.
[13] GUAN Qing-feng, ZOU Yang, ZHANG Zai-qiang, GUAN Jin-tong, SU Jing-xin, WANG Zhi-ping. Microstructures and corrosion property of pure copper under high-current pulsed electron beam irradiation [J]. 吉林大学学报(工学版), 2013, 43(04): 964-969.
[14] RUAN De-wen, SUDAGAR Jothi, LIANG Ya-qin, ELANSEZHIAN Rasu, LIAN Jian-she. Effects of surfactants on corrosion behavior of chromium-free electroless nickel deposit on magnesium alloy [J]. 吉林大学学报(工学版), 2013, 43(02): 363-367.
[15] YANG Yue, CHEN Bin. Effects of SiC nano-particles on microstructure and the corrosion resistance of micro-arc oxidation films produced on aluminium alloy [J]. 吉林大学学报(工学版), 2011, 41(增刊1): 106-110.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
Copyright © Journal of Jilin University(Engineering and Technology Edition), All Rights Reserved.
Tel: +86-431-85095297　Fax: +86-431-85094074　E-mail: xbgxb@jlu.edu.cn
Powered by Beijing Magtech Co. Ltd