吉林大学学报(工学版) ›› 2013, Vol. 43 ›› Issue (03): 677-681.doi: 10.7964/jdxbgxb201303020

• 论文 • 上一篇    下一篇

二辊矫直过程导板间距工艺参数分析

王云1, 刘才1, 马立东2, 王玉峰3, 黄庆学2   

  1. 1. 燕山大学 机械工程学院,河北 秦皇岛 066004;
    2. 太原科技大学 重型机械教育部工程研究中心,太原 030024;
    3. 石家庄钢铁有限责任公司 新一轧厂, 石家庄 050031
  • 收稿日期:2012-06-19 出版日期:2013-05-01 发布日期:2013-05-01
  • 作者简介:王云(1983-),男,博士研究生.研究方向:二辊矫直机及矫直工艺.E-mail:wtowy521@163.com
  • 基金资助:

    "973"国家重点基础研究发展计划项目(2011CB612204);国家自然科学基金项目(51105264,51104104).

Analysis of interval between guides during two-roll straightening process

WANG Yun1, LIU Cai1, MA Li-dong2, WANG Yu-feng3, HUANG Qing-xue2   

  1. 1. College of Mechanical Engineering, Yanshan University, Qinhuangdao 066004, China;
    2. Heavy Machinery Engineering Research Center of the Ministry of Education, Taiyuan University of Science and Technology, Taiyuan 030024, China;
    3. New No.1 Rolling Mill of Shijiazhuang I.&S. Co., Ltd, Shijiazhuang 050031, China
  • Received:2012-06-19 Online:2013-05-01 Published:2013-05-01

RICH HTML

0   

PDF (PC)

333

摘要： 针对某钢厂棒材矫直过程中二辊矫直机导板间距没有明确规定并且导板磨损严重的情况,用大型非线性有限元软件建立了棒材二辊矫直过程的三维弹塑性有限元模型.基于此模型研究了不同导板间距下矫直力、导板支撑力、塑性变形程度、矫后残余应力及最大挠度的变化规律,综合分析提出了合理的导板间距取值范围.新的导板间距比之前实际应用的值有所增大,应用后导板更换频率降低.

关键词: 金属材料, 轧制, 二辊矫直, 导板间距

Abstract: As reasonable interval between guides during two-roll straightening process was not easy to determine, a 3D elastic-plastic finite element model of the straightening process of bar material was proposed. Based on this model, variations of straightening force, supporting force of guides, degree of plastic deformation, residual stress and the maximum deflection of the bar after straightening were analyzed in different intervals. Reasonable range of interval between guides was determined by comprehensive consideration. The obtained range of interval by this study is larger than previously used range, and the frequency of change of guides is decreased.

Key words: metallic materials, rolling, two-roll straightening, interval between guides

中图分类号: 

  • TG335.21
[1] 崔甫. 矫直原理与矫直机械[M]. 北京:冶金工业出版社,2007.

[2] Mutrux A, Berisha B, Hochholdinger B, et al. Numerical modelling of cross roll straightening//Proceedings of the 7th LS-Dyna Anwederforum, Bamberg, Germany, 2008: C-I-33-C-I-40.

[3] Mutrux A, Berisha B, Weber M, et al. FE simulation of cross roll straightening: a submodel approach//Proceedings of the 10th International Conference on Computational Plasticity(COMPLAS X), Barcelona, Spain, 2009.

[4] Mutrux A, Berisha B, Hora P. Prediction of cyclic softening in a medium carbon steel during cross roll straightening[J]. Journal of Materials Processing Technology, 2011, 211(8): 1448-1456.

[5] Mutrux A, Berisha B, Hora P. FE simulation of cross roll straightening: a strain tensor field approach//Proceedings of the 10th International Conference on Numerical Methods in Industrial Forming Processes (NUMIFORM 2010), Pohang, Korea, 2010: 941-948.

[6] Asakawa M, Urabe M, Nishimura K, et al. Theoretical and experimental analysis of roller leveller straightening for coiled bar[J]. Steel Res Int, 2010, 81(9): 242-245.

[7] Kuboki K, Huang H, Murata M, et al. FEM analysis of tube straightener adopting implicit scheme[J]. Steel Res Int, 2010, 81(9): 584-587.

[8] Das Talukder N K, Singh A N. Mechanics of bar straightening, Part 1: general analysis of straightening process[J]. Trans ASME, 1991, 113(2): 224-227.

[9] Das Talukder N K, Singh A N. Mechanics of bar straightening, Part 2: straightening in cross-roll straighteners[J]. Trans ASME, 1991, 113(2): 228-232.

[10] Wu B J, Chan T C, Lee T C, et al. A study on the precision modeling of the bars produced in two cross-roll straightening[J]. Mater Process Tech, 2000, 99(1-3): 202-206.

[11] 刘志亮. 棒材二辊矫直机辊型及变形机理研究. 秦皇岛: 燕山大学机械工程学院, 2009. Liu Zhi-liang. Study on mechanism and roller shape for two-roller bar straightener. Qinhuangdao: College of Mechanical Engineering,Yanshan University, 2009.

[12] 刘勇,双远华,贾海亮,等. 二辊矫直过程工艺参数研究[J]. 重型机械, 2011(6): 31-35. Liu Yong, Shuang Yuan-hua, Jia hai-liang, et al. Study on straightening technological parameters for two-roll straightener production process[J]. Heavy Machinery, 2011(6): 31-35.

[13] 崔甫. 矫直技术与理论的新探索[M]. 北京:冶金工业出版社,2010: 73-91.

[14] 陈惠发,A.F.萨里普. 弹性与塑性力学[M]. 北京:中国建筑工业出版社,2003: 273-276.
[1] 关庆丰,张福涛,彭韬,吕鹏,李姚君,许亮,丁佐军. 含硼、钴9%Cr耐热钢的热变形行为[J]. 吉林大学学报(工学版), 2018, 48(6): 1799-1805.
[2] 关庆丰, 董书恒, 郑欢欢, 李晨, 张从林, 吕鹏. 强流脉冲电子束作用下45#钢表面Cr合金化[J]. 吉林大学学报(工学版), 2018, 48(4): 1161-1168.
[3] 赵宇光, 杨雪慧, 徐晓峰, 张阳阳, 宁玉恒. Al-10Sr变质剂状态、变质温度及变质时间对ZL114A合金组织的影响[J]. 吉林大学学报(工学版), 2018, 48(1): 212-220.
[4] 汤华国, 马贤锋, 赵伟, 刘建伟, 赵振业. 高性能金属铝的制备、微观结构及其热稳定性[J]. 吉林大学学报(工学版), 2017, 47(5): 1542-1547.
[5] 关庆丰, 张远望, 孙潇, 张超仁, 吕鹏, 张从林. 强流脉冲电子束作用下铝钨合金的表面合金化[J]. 吉林大学学报(工学版), 2017, 47(4): 1171-1178.
[6] 伦凤艳, 付文智, 李明哲, 依卓, 王欣桐, 陈雪. 基于弯曲辊的三维曲面柔性轧制成形[J]. 吉林大学学报(工学版), 2017, 47(3): 876-883.
[7] 杨晓红, 杭文先, 秦绍刚, 刘勇兵, 刘利萍. H13钢激光熔覆钴基复合涂层的组织及耐磨性[J]. 吉林大学学报(工学版), 2017, 47(3): 891-899.
[8] 关庆丰, 黄尉, 李怀福, 龚晓花, 张从林, 吕鹏. 强流脉冲电子束诱发的Cu-C扩散合金化[J]. 吉林大学学报(工学版), 2016, 46(6): 1967-1973.
[9] 张学广, 刘纯国, 郑愿, 江仲海, 李湘吉. 基于延性损伤和剪切损伤的铝合金成形极限预测[J]. 吉林大学学报(工学版), 2016, 46(5): 1558-1566.
[10] 刘晓波, 周德坤, 赵宇光. 不同等温热处理条件下半固态挤压Mg2Si/Al复合材料的组织和性能[J]. 吉林大学学报(工学版), 2016, 46(5): 1577-1582.
[11] 赵世喆, 周宏, 佟国栋, 李文平, 关峰. AZ31合金的平均晶粒尺寸与单道次轧制变形量之间的量化关系[J]. 吉林大学学报(工学版), 2016, 46(2): 505-510.
[12] 李春玲, 樊丁, 王斌, 余淑荣. 5A06铝合金/镀锌钢预置涂粉对接激光熔钎焊组织与性能[J]. 吉林大学学报(工学版), 2016, 46(2): 516-521.
[13] 张家陶, 赵宇光, 谭娟. 初始组织对电脉冲处理逆变奥氏体晶粒细化效果的影响[J]. 吉林大学学报(工学版), 2016, 46(1): 193-198.
[14] 张志强， 贾晓飞， 袁秋菊. 基于Yoshida-Uemori模型的TRIP800高强钢回弹分析[J]. 吉林大学学报(工学版), 2015, 45(6): 1852-1856.
[15] 张志强, 贾晓飞, 赵勇, 李湘吉. 高强度硼钢淬火界面热交换系数的实验与模拟[J]. 吉林大学学报(工学版), 2015, 45(4): 1195-1199.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
版权所有 © 《吉林大学学报(工学版)》编辑部
地址：长春市人民大街5988号　电话：+86-431-85095297　传真：+86-431-85094074　E-mail: xbgxb@jlu.edu.cn
本系统由北京玛格泰克科技发展有限公司设计开发