掺锂渣再生混凝土三点弯曲梁双K断裂特性

doi:10.13229/j.cnki.jdxbgxb20200590

摘要/Abstract

摘要：

为研究锂渣掺量和再生粗骨料取代率对掺锂渣再生混凝土双K断裂韧度的影响规律，试验制作了锂渣掺量分别为0%、10%、20%和再生粗骨料取代率分别为0%、30%、50%的9组配比36根掺锂渣再生混凝土标准三点弯曲梁进行断裂测试，并在分析裂缝扩展过程的基础上提出了混凝土断裂韧度预估模型。试验结果表明：随着再生粗骨料取代率的增大，混凝土双K断裂韧度均呈现先增大、后减小的趋势；锂渣的掺入可以提高混凝土的双K断裂韧度，且在一定程度上弥补高再生粗骨料取代率导致混凝土断裂韧度小的不足；锂渣掺量为20%、再生粗骨料取代率为30%时，混凝土双K断裂特性最优，起裂韧度和失稳韧度分别为0.54 MPa·m^1/2和1.07 MPa·m^1/2，较基准组分别提高了42.1%和23%。

关键词: 锂渣, 再生粗骨料, 三点弯曲梁, 双K断裂韧度

Abstract:

To study the effects of different lithium slag contents and recycled coarse aggregate percentages on the double-K fracture toughness of recycled concrete with lithium slag, 36 standard three-point bending beams of recycled concrete with lithium slag, which include 9 mix ratios about lithium slag content of 0%,10%,20% and recycled coarse aggregate percentage of 0%,30%,50%, were prepared for fracture test. Based on the analysis of crack propagation process, a prediction model for fracture toughness of concrete was proposed. The research results show that the double K fracture toughness of concrete all increases first and then decreases with the increase of the recycled coarse aggregate percentage. The addition of lithium slag can improve the double K fracture toughness of the concrete and offset the deficiency of the concrete fracture performance with high recycled coarse aggregate percentage. The double K properties are optimal when the lithium slag content and recycled coarse aggregate account for 20 % and 30 % respectively. The initial fracture toughness and unstable fracture toughness reach 0.54 MPa·m^1/2 and1.07 MPa·m^1/2, increasing by 42.1% and 23 % respectively compared with the reference group.

Key words: lithium slag, recycled coarse aggregate, three point bending beam, double-K fracture toughness

中图分类号:

TU528

秦拥军,陈楠,蔺鹏杰,于江. 掺锂渣再生混凝土三点弯曲梁双K断裂特性[J]. 吉林大学学报(工学版), 2021, 51(6): 2121-2127.

Yong-jun QIN,Nan CHEN,Peng-jie LIN,Jiang YU. Double K fracture characteristics of recycled concrete three⁃point bending beam mixed with lithium slag[J]. Journal of Jilin University(Engineering and Technology Edition), 2021, 51(6): 2121-2127.

图/表 12

表1

表2

表3

图1

图2

图3

表4

双K断裂模型计算的断裂参数"

编号	试件数量	P_ini/kN	P_max/kN	CMOD/μm	E/GPa	a_c/mm	$K I c i n i$ /（MPa· $m 1 / 2$ ）	$K I c u n$ /（MPa· $m 1 / 2$
LS-RC-1	4	1.52	2.46	44.56	29.3	50	0.38	0.87
LS-RC-2	4	1.76	2.66	46.21	31.0	52	0.44	0.93
LS-RC-3	4	1.82	2.90	48.34	30.7	51	0.44	0.95
LS-RC-4	4	1.75	2.58	46.28	31.1	52	0.44	0.93
LS-RC-5	4	1.9	2.77	49.67	31.5	53	0.48	1.03
LS-RC-6	4	2.15	2.97	51.93	31.9	52	0.54	1.07
LS-RC-7	4	1.48	2.37	46.28	28.6	51	0.37	0.83
LS-RC-8	4	1.57	2.58	50.75	29.0	52	0.39	0.96
LS-RC-9	4	1.64	2.73	52.15	30.6	51	0.41	1.01

表4

图4

图5

图6

图7

图8

参考文献 13

1	肖建庄. 再生混凝土[M]. 北京:中国建筑工业出版社,2008.
2	秦拥军,严文龙,于江. 掺锂渣再生混凝土弹性模量及应力-应变曲线试验[J].科学技术与工程,2016,16(16):254-262.
	Qin Yong-jun, Yan Wen-long, Yu Jiang. Elastic modulus and stress-strain curve test of recycled concrete with lithium slag[J]. Science Technology and Engineering, 2016,16(16):254-262.
3	秦拥军,李振兴,侯勇辉,等. 掺杂锂渣再生混凝土轴压长柱受压性能试验研究[J].武汉理工大学学报,2017,39(3):65-70.
	Qin Yong-jun, Li Zhen-xing, Hou Yong-hui, et al. Experimental study on compressive performance of doped lithium slag axial recycled concrete long columns[J]. Journal of Wuhan University of Technology, 2017,39(3):65-70.
4	Qin Y J, Chen J J, Li Z X, et al. The mechanical properties of recycled coarse aggregate concrete with lithium slag[J]. Advances in Materials Science and Engineering, 2019, 2019 (1): 1-12.
5	陈洁静,秦拥军,肖建庄,等. 基于CT技术的掺锂渣再生混凝土孔隙特征研究[J/OL]. [2020-10-30].
6	河海大学. DL/T 5332—2005, 水工混凝土断裂试验规程[M]. 北京:中国电力出版社,2006.
7	李晓东,董伟,吴智敏,等. 小尺寸混凝土试件双K断裂参数试验研究[J]. 工程力学,2010, 27(2):166-171, 185.
	Li Xiao-dong, Dong Wei, Wu Zhi-min, et al. Experimental investigation on double-K fracture parameters for small size specimens of concrete[J]. Engineering Mechanics, 2010,27(2): 166-171, 185.
8	胡少伟,米正祥. 标准钢筋混凝土三点弯曲梁双K断裂特性试验研究[J]. 建筑结构学报,2013,34(3):152-157.
	Hu Shao-wei, Mi Zheng-xiang. Experimental study on double-K fracture characteristics of standard reinforced concrete three-point beam[J]. Journal of Building Structures, 2013,34(3):152-157.
9	罗素蓉,白俊杰. 纳米改性对再生混凝土双K断裂参数的影响[J]. 水利学报,2018,49(6):670-677.
	Luo Su-rong, Bai Jun-jie. Effect of nanometer modification on double K fracture parameters of recycled concrete[J]. Journal of Hydraulic Engineering,2018,49(6):670-677.
10	梁宁慧,缪庆旭,刘新荣,等. 聚丙烯纤维增强混凝土断裂韧度及软化本构曲线确定[J]. 吉林大学学报:工学版,2019,49(4):1144-1152.
	Liang Ning-hui, Miao Qing-xu, Liu Xin-rong, et al. Determination of fracture toughness and softening traction separation law of polypropylene fiber reinforced concrete[J]. Journal of Jilin University (Engineering and Technology Edition),2019,49(4): 1144-1152.
11	. 混凝土用再生粗骨料[S].
12	徐世烺. 混凝土断裂力学[M].北京:科学出版社, 2011.
13	李丽丹. 黏聚力模型在混凝土裂纹扩展中的应用[D]. 武汉:武汉科技大学理学院, 2015.
	Li Li-dan. Application of cohesive traction crack model in crack propagation in concrete[D]. Wuhan:Faculty of Science, Wuhan University of Science and Technology,2015.

相关文章 15

[1]	李艺,苏悦琦. 基于不同孔径范围的碳化作用下纤维混凝土的气体渗透性能和细观结构[J]. 吉林大学学报(工学版), 2021, 51(4): 1287-1295.
[2]	张广泰,张路杨,邢国华,曹银龙,易宝. 钢-聚丙烯混杂纤维混凝土剪力墙抗震性能[J]. 吉林大学学报(工学版), 2021, 51(3): 946-955.
[3]	刘寒冰,高鑫,宫亚峰,刘诗琪,李文俊. 表面处理对玄武岩纤维活性粉末混凝土力学性能的影响及断裂特性[J]. 吉林大学学报(工学版), 2021, 51(3): 936-945.
[4]	何娟,程从密,杨毅男,张亚芳,钟明峰. 湿热养护时掺合料对玻纤增强水泥性能的影响[J]. 吉林大学学报(工学版), 2020, 50(2): 648-653.
[5]	王鹏辉,乔宏霞,冯琼,曹辉,温少勇. 氯氧镁涂层钢筋混凝土两重因素耦合作用下的耐久性模型[J]. 吉林大学学报(工学版), 2020, 50(1): 191-201.
[6]	狄胜同,贾超,乔卫国,李康,童凯. 橡胶集料混凝土细观损伤特性的加载速率效应[J]. 吉林大学学报(工学版), 2019, 49(6): 1900-1910.
[7]	梁宁慧,缪庆旭,刘新荣,代继飞,钟祖良. 聚丙烯纤维增强混凝土断裂韧度及软化本构曲线确定[J]. 吉林大学学报(工学版), 2019, 49(4): 1144-1152.
[8]	李静, 王哲. 真三轴加载条件下混凝土的力学特性[J]. 吉林大学学报(工学版), 2017, 47(3): 771-777.
[9]	张静, 刘向东. 混沌粒子群算法优化最小二乘支持向量机的混凝土强度预测[J]. 吉林大学学报(工学版), 2016, 46(4): 1097-1102.
[10]	高小建, 孙博超, 叶焕, 王子龙. 矿物掺合料对自密实混凝土流变性能的影响[J]. 吉林大学学报(工学版), 2016, 46(2): 439-444.
[11]	柳俊哲, 袁伟静, 贺智敏, 巴明芳, 陈剑斌. 碳化对混凝土碱骨料反应的影响[J]. 吉林大学学报(工学版), 2015, 45(3): 783-787.
[12]	宿晓萍，王清. 复合盐浸-冻融-干湿多因素作用下的混凝土腐蚀破坏[J]. 吉林大学学报(工学版), 2015, 45(1): 112-120.
[13]	王甲春, 阎培渝. 海洋环境下钢筋混凝土中钢筋锈蚀的概率[J]. 吉林大学学报(工学版), 2014, 44(2): 352-357.
[14]	肖锐, 邓宗才, 兰明章, 申臣良. 不掺硅粉的活性粉末混凝土配合比试验[J]. 吉林大学学报(工学版), 2013, 43(03): 671-676.
[15]	高小建,阚雪峰,杨英姿. 单面干燥条件下掺硅灰混凝土的收缩变形分布[J]. 吉林大学学报(工学版), 2010, 40(03): 694-0698.

Metrics

Viewed

Full text

Abstract

Cited

Shared

Discussed

材料	CaO	SiO₂	Al₂O₃	Li₂O	Loss	Fe₂O₃	SO₃
水泥	60.23	21.26	5.03	-	2.17	3.24	2.65
锂渣	7.99	54.40	19.81	0.18	6.72	1.41	8.31

粗骨料类别	微粉含量/%	吸水率/%	针片状含量/%	坚固性/%	表观密度/（kg·m^-3）
天然	0.3	0.5	5	1	2640
再生	0.5	3.46	2	4.2	2825

编号	RC/%	LS/%	混凝土配合比/（kg·m^-3）							28 d抗压强度/MPa	劈裂拉强度/MPa
编号	RC/%	LS/%	锂渣	再生粗骨料	净用水	砂	卵石	水泥	附加用水	28 d抗压强度/MPa	劈裂拉强度/MPa
LS-RC-1	0	0	0	0	195	523.5	1221.4	433.0	0	34.72	3.38
LS-RC-2	0	10	43.3	0	195	523.5	1221.4	389.7	0	36.46	4.06
LS-RC-3	0	20	86.6	0	195	523.5	1221.4	346.4	0	40.58	4.27
LS-RC-4	30	0	0	366.4	195	523.5	854.9	433.0	7.84	42.09	3.82
LS-RC-5	30	10	43.3	366.4	195	523.5	854.9	389.7	7.84	44.62	4.23
LS-RC-6	30	20	86.6	366.4	195	523.5	854.9	346.4	7.84	47.53	4.38
LS-RC-7	50	0	0	610.7	195	523.5	610.7	433.0	13.07	37.24	3.56
LS-RC-8	50	10	43.4	610.7	195	523.5	610.7	389.7	13.07	40.86	4.03
LS-RC-9	50	20	86.6	610.7	195	523.5	610.7	346.4	13.07	42.83	4.19