基于Yoshida-Uemori模型的TRIP800高强钢回弹分析

张志强， 贾晓飞， 袁秋菊   

  1. 吉林大学 材料科学与工程学院,长春 130022
  • 收稿日期:2014-05-09 出版日期:2015-11-01 发布日期:2015-11-01
  • 作者简介:张志强(1977-),男,副教授,博士.研究方向:高强度钢板精密成形技术.E-mail:zhangzq@jlu.edu.cn
  • 基金资助:
    国家自然科学基金项目(51205162)

Springback analysis of trip high strength steel based on Yoshida-Uemori model

ZHANG Zhi-qiang, JIA Xiao-fei, YUAN Qiu-ju   

  1. College of Material Science and Engineering, Jilin University, Changchun 130022,China
  • Received:2014-05-09 Online:2015-11-01 Published:2015-11-01

RICH HTML

1   

PDF (PC)

795

摘要： 利用自行研制的试验装置进行了TRIP800高强钢的平面拉伸压缩试验,建立了TRIP800高强钢Yoshida-Uemori(Y-U)硬化模型,并对该模型进行了验证。在此基础上,进行了U形件冲压回弹分析,结果表明:基于Y-U材料硬化模型的U形件回弹比等向硬化模型具有更大的回弹值。

关键词: 金属材料, TRIP高强钢, 平面拉伸压缩, Yoshida-Uemori材料模型, 回弹

Abstract: In-plane tension-compression experiments of TRIP800 steel were conducted with a self-developed device. Based on the experiments, the Yoshida-Uemori (Y-U) hardening model was built and verified, which was then used to analyze the springback of the U-shaped part. The results show that more springback is achieved on the Y-U model than that based on isotropic model.

Key words: metal material, TRIP high strength steel, in-plane tension-compression tests, Yoshida-Uemori model, springback

中图分类号: 

  • TG386.4
[1] 马鸣图,易红亮. 高强度钢在汽车制造中的应用[J]. 金属热处理,2011,26(6):9-20.
Ma Ming-tu, Yi Hong-liang. Application of high strength to manufacturing auto[J]. Heat Treatment, 2011,26(6):9-20.
[2] 康永林,陈贵江,朱国明,等. 新一代汽车用先进高强钢的成形与应用[J]. 钢铁,2010,45(8):1-6,19.
Kang Yong-lin, Chen Gui-jiang, Zhu Guo-ming, et al. Forming technology and application of generation advanced high strength steel for automobile[J]. Iron and Steel,2010, 45(8):1-6,19.
[3] 米振莉,李志超,范东亮,等. 高强度冷轧TRIP钢的工艺改进及组织性能[J]. 材料热处理学报, 2011,32(10):112-116.
Mi Zhen-li, Li Zhi-chao, Fan Dong-liang, et al. Influence of heat treatment on microstructure and properties of a high strength cold-roll trip steel[J]. Transactions of Materials and Heat Treatment,2011,32(10):112-116.
[4] 路洪洲,李斌,吴娥梅,等. 汽车用高强度TRIP钢组织性能及成形工艺[J]. 精密成形工程,2012,4(2):6-9.
Lu Hong-zhou,Li Bin, Wu E-mei,et al. The microstructure properties and forming process of high strength automotive TRIP steel[J]. Journal of Netshape Forming Engineering,2012,4(2):6-9.
[5] 胡康康,彭雄奇,陈军,等. 基于Yoshida-Uemori材料模型的汽车结构件冲压回弹分析[J]. 材料科学与工艺,2011,19(6):43-47.
Hu Kang-kang, Peng Xiong-qi, Chen Jun, et al. Springback prediction of automobile body panel based on Yoshida-Uemori material model[J]. Materials Science&Technology, 2011,19(6):43-47.
[6] 胡轶敏,林忠钦,徐伟力,等.车身覆盖件冲压成形动态仿真的研究进展[J].力学进展,2000,30(2):252-271.
Hu Yi-min,Lin Zhong-qin,Xu Wei-li,et al.Advances in dynamic simulation of stamping of autobody pane[J].Advances in Mechanics,2000,30(2):252-271.
[7] 李泷杲,王书恒,徐岩. 金属板料成形有限元模拟基础-PAMSTAMP2G[M]. 北京:北京航空航天大学出版社,2008.
[8] Yoshida F, Uemori T, Fujiwara K. Elastic-plastic behavior of steel sheets under in-plane cyclic tension-compression at large strain[J]. International Journal of Plasticity,2002,18(5-6):633-659.
[9] Yoshida F, Uemori T. A model of large-strain cyclic plasticity describing the Bauschinger effect and work-hardening stagnation[J]. International Journal of Plasticity, 2002,18(5-6):661-686.
[10] Yoshida F, Uemori T. A model of large-strain cyclic plasticity and its application to spring-back simulation[J]. International Journal of Mechanical Sciences, 2003,45(10):1687-1702.
[11] 张璐,陈劼实,陈军. 基于Yoshida-Uemori硬化模型的高强钢冲压件回弹预测研究[J]. 模具技术,2012(3):11-14,21.
Zhang Lu,Chen Jie-shi,Chen Jun. Springback prediction of advanced high strength part based on Yoshida-Uemori hardening model[J]. Die and Mould Technology,2012(3):11-14,21.
[1] 关庆丰,张福涛,彭韬,吕鹏,李姚君,许亮,丁佐军. 含硼、钴9%Cr耐热钢的热变形行为[J]. 吉林大学学报(工学版), 2018, 48(6): 1799-1805.
[2] 关庆丰, 董书恒, 郑欢欢, 李晨, 张从林, 吕鹏. 强流脉冲电子束作用下45#钢表面Cr合金化[J]. 吉林大学学报(工学版), 2018, 48(4): 1161-1168.
[3] 赵宇光, 杨雪慧, 徐晓峰, 张阳阳, 宁玉恒. Al-10Sr变质剂状态、变质温度及变质时间对ZL114A合金组织的影响[J]. 吉林大学学报(工学版), 2018, 48(1): 212-220.
[4] 付文智, 刘晓东, 王洪波, 闫德俊, 刘晓莉, 李明哲, 董玉其, 曾振华, 刘桂彬. 关于1561铝合金曲面件的多点成形工艺[J]. 吉林大学学报(工学版), 2017, 47(6): 1822-1828.
[5] 张志强, 刘从豪, 何东野, 李湘吉, 李纪萱. 基于性能梯度分布的硼钢热冲压工艺对形状精度的影响[J]. 吉林大学学报(工学版), 2017, 47(6): 1829-1833.
[6] 王辉, 周杰, 熊煜, 陶亚平, 向荣. 基于逆向工程的复杂曲面冲压件回弹补偿[J]. 吉林大学学报(工学版), 2017, 47(6): 1842-1847.
[7] 汤华国, 马贤锋, 赵伟, 刘建伟, 赵振业. 高性能金属铝的制备、微观结构及其热稳定性[J]. 吉林大学学报(工学版), 2017, 47(5): 1542-1547.
[8] 关庆丰, 张远望, 孙潇, 张超仁, 吕鹏, 张从林. 强流脉冲电子束作用下铝钨合金的表面合金化[J]. 吉林大学学报(工学版), 2017, 47(4): 1171-1178.
[9] 杨晓红, 杭文先, 秦绍刚, 刘勇兵, 刘利萍. H13钢激光熔覆钴基复合涂层的组织及耐磨性[J]. 吉林大学学报(工学版), 2017, 47(3): 891-899.
[10] 梁继才, 李义, 高嵩, 滕菲. 型材多点柔性拉弯成形回弹预测[J]. 吉林大学学报(工学版), 2017, 47(1): 185-190.
[11] 关庆丰, 黄尉, 李怀福, 龚晓花, 张从林, 吕鹏. 强流脉冲电子束诱发的Cu-C扩散合金化[J]. 吉林大学学报(工学版), 2016, 46(6): 1967-1973.
[12] 张学广, 刘纯国, 郑愿, 江仲海, 李湘吉. 基于延性损伤和剪切损伤的铝合金成形极限预测[J]. 吉林大学学报(工学版), 2016, 46(5): 1558-1566.
[13] 刘晓波, 周德坤, 赵宇光. 不同等温热处理条件下半固态挤压Mg2Si/Al复合材料的组织和性能[J]. 吉林大学学报(工学版), 2016, 46(5): 1577-1582.
[14] 李春玲, 樊丁, 王斌, 余淑荣. 5A06铝合金/镀锌钢预置涂粉对接激光熔钎焊组织与性能[J]. 吉林大学学报(工学版), 2016, 46(2): 516-521.
[15] 张家陶, 赵宇光, 谭娟. 初始组织对电脉冲处理逆变奥氏体晶粒细化效果的影响[J]. 吉林大学学报(工学版), 2016, 46(1): 193-198.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
版权所有 © 《吉林大学学报(工学版)》编辑部
地址：长春市人民大街5988号　电话：+86-431-85095297　传真：+86-431-85094074　E-mail: xbgxb@jlu.edu.cn
本系统由北京玛格泰克科技发展有限公司设计开发