doi:10.7964/jdxbgxb201305028

吉林大学学报(工学版) ›› 2013, Vol. 43 ›› Issue (05): 1320-1324.doi: 10.7964/jdxbgxb201305028

中碳钢温变形过程的流变应力

李志杰^1,2, 彭艳^1,2, 刘宏民^1,2, 王素芬¹, 肖力子¹

1. 燕山大学国家冷轧板带装备及工艺工程技术研究中心, 河北秦皇岛 066004;
2. 燕山大学亚稳材料制备技术与科学国家重点实验室, 河北秦皇岛 066004

收稿日期:2012-04-06 出版日期:2013-09-01 发布日期:2013-09-01
通讯作者: 彭艳(1971- ),男,教授,博士生导师.研究方向:金属轧制成形与组织性能控制.E-mail:pengyan@ysu.edu.cn E-mail:pengyan@ysu.edu.cn
作者简介:李志杰(1979- ),男,博士研究生.研究方向:金属轧制成形与组织性能控制.E-mail:lizhijie09@yahoo.com.cn
基金资助:
国家科技支撑计划项目(2011BAF15B01);教育部新世纪优秀人才计划项目(NCET-09-0117);国家科技重大专项项目(2011ZX04002-101);河北省科技计划项目(10212101D).

Flow stress of medium carbon steel under warm compression deformation

LI Zhi-jie^1,2, PENG Yan^1,2, LIU Hong-min^1,2, WANG Su-fen¹, XIAO Li-zi¹

1. National Engineering Research Center for Equipment and Technology of Cold Strip Rolling, Yanshan University, Qinhuangdao 066004, China;
2. State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004, China

Received:2012-04-06 Online:2013-09-01 Published:2013-09-01

摘要/Abstract

摘要：

为了制定中碳钢温轧工艺,利用Gleeble-3500热模拟试验机对中碳钢进行温压缩试验,研究其在不同变形温度(550~700 ℃)和应变速率(0.001~10 s^-1)下的流变行为,讨论温变形过程流变应力的影响因素。研究结果表明:中碳钢温变形过程由铁素体动态回复、铁素体动态再结晶、渗碳体球化和稳态变形4个阶段构成,其软化机理主要有铁素体动态再结晶和珠光体动态球化。

关键词: 金属材料, 中碳钢, 温变形, 流变应力

Abstract:

In order to design the warm rolling process of medium carbon steel, flow stress under warm compression deformation was investigated by experiments. The experiments were carried out on a Gleeble-3500 thermal simulation machine at temperature of 550~700 ℃ with constant strain rates 0.001~1 s^-1. The influence factors in warm deformation were studied. Results show that the stress-strain curve of medium carbon steel under warm deformation is composed of four stages: the ferrite dynamic recovery, ferrite dynamic recrystallization, cementite spheroidization, and steady deformation state. The main soften mechanisms are ferrite dynamic recrystallization and pearlite dynamic spheroidization.

Key words: metal material, medium carbon steel, warm deformation, flow-stress

中图分类号:

TG142

李志杰, 彭艳, 刘宏民, 王素芬, 肖力子. 中碳钢温变形过程的流变应力[J]. 吉林大学学报(工学版), 2013, 43(05): 1320-1324.

LI Zhi-jie, PENG Yan, LIU Hong-min, WANG Su-fen, XIAO Li-zi. Flow stress of medium carbon steel under warm compression deformation[J]. 吉林大学学报(工学版), 2013, 43(05): 1320-1324.

参考文献

[1] 徐匡迪. 低碳经济与钢铁工业[J]. 钢铁, 2010, 45(3): 1-12. Xu Kuang-di. Low carbon economy and iron and steel industry[J]. Iron and Steel, 2010, 45(3): 1-12.

[2] 董瀚,王毛球,翁宇庆. 高性能钢的M3组织调控理论与技术[J]. 钢铁, 2010, 45(7): 1-7. Dong Han, Wang Mao-qiu, Weng Yu-qing. Performance improvement of steels through M3 structure control[J]. Iron and Steel, 2010, 45(7): 1-7.

[3] Yunusova N F, Islamgaliev R K, Bardinova M A, et al. Microstructure and mechanical properties of aluminum alloy 1421 after ECAP and warm rolling[J]. Metal Science and Heat Treatment, 2007, 49(3/4): 135-140.

[4] Stolyarov V V, Zhu Y T, Alexandrov I V, et al. Grain refinement and properties of pure Ti processed by warm ECAP and cold rolling[J]. Materials Science and Engineering: A, 2003, 343(1/2): 43-50.

[5] 周纪华,管克智.金属塑性变形阻力[M]. 北京: 机械工业出版社, 1989.

[6] 姚圣杰,杜林秀,王国栋. 温轧低碳钢渗碳体形态对终轧组织性能的影响[J]. 材料热处理学报, 2010, 31(3): 59-63. Yao Sheng-jie, Du Lin-xiu, Wang Guo-dong. Effect of cementite morphology in a warm-rolled low-carbon steel on its microstructure and properties after finish rolling[J]. Transactions of Metals and Heat Treatment, 2010, 31(3): 59-63.

[7] 熊毅,陈正阁,厉勇,等. 温压缩变形过程中渗碳体的球化行为[J]. 材料热处理学报, 2008, 29(1): 42-46. Xiong Yi, Chen Zheng-ge,Li Yong, et al. Spheroidization behavior of cementite during warm compression deformation[J]. Transactions of Metals and Heat Treatment,2008, 29(1): 42-46.

[8] 谭洪锋,杨王玥,陈国安. 初始组织形态对中碳钢温变形组织演变的影响[J]. 北京科技大学学报, 2008, 30(4): 368-373. Tan Hong-feng, Yang Wang-yue, Chen Guo-an. Effect of initial microstructure on the microstructure evolution of medium carbon steel during warm deformation[J]. Journal of University of Science and Technology Beijing, 2008, 30(4): 368-373.

[9] Storojeva L, Kaspar R, Ponge D. Effects of heavy warm deformation on microstructure and mechanical properties of a medium carbon ferritic-pearlitic steel[J]. ISIJ International, 2004, 44(7): 1211-1216.

[10] Timokhina I B, Nosenkov A I, Humphreys A O, et al. Effect of alloying elements on the microstructure and texture of warm rolled steels[J]. ISIJ International, 2004, 44(4): 717-724.

[11] 赫尔 D,培根 D. 位错导论[M]. 丁树深,李齐,译.北京: 科学出版社, 1990.

[12] Solhjoo S, Ebrahimi R. Prediction of no-recrystallization temperature by simulation of multi-pass flow stress curves from single-pass curves[J]. Journal of Materials Science, 2010, 45(21): 5960-5966.

[13] Suwas S, Beausir B, Tóth L S, et al. Texture evolution in commercially pure titanium after warm equal channel angular extrusion[J]. Acta Materialia, 2011, 59(3): 1121-1133.

[14] Dudova N, Belyakov A, Sakai T, et al. Dynamic recrystallization mechanisms operating in a Ni-20%Cr alloy under hot-to-warm working[J]. Acta Materialia, 2010, 58(10): 3624-3632.

相关文章 15

[1]	关庆丰,张福涛,彭韬,吕鹏,李姚君,许亮,丁佐军. 含硼、钴9%Cr耐热钢的热变形行为[J]. 吉林大学学报(工学版), 2018, 48(6): 1799-1805.
[2]	关庆丰, 董书恒, 郑欢欢, 李晨, 张从林, 吕鹏. 强流脉冲电子束作用下45#钢表面Cr合金化[J]. 吉林大学学报(工学版), 2018, 48(4): 1161-1168.
[3]	赵宇光, 杨雪慧, 徐晓峰, 张阳阳, 宁玉恒. Al-10Sr变质剂状态、变质温度及变质时间对ZL114A合金组织的影响[J]. 吉林大学学报(工学版), 2018, 48(1): 212-220.
[4]	汤华国, 马贤锋, 赵伟, 刘建伟, 赵振业. 高性能金属铝的制备、微观结构及其热稳定性[J]. 吉林大学学报(工学版), 2017, 47(5): 1542-1547.
[5]	关庆丰, 张远望, 孙潇, 张超仁, 吕鹏, 张从林. 强流脉冲电子束作用下铝钨合金的表面合金化[J]. 吉林大学学报(工学版), 2017, 47(4): 1171-1178.
[6]	杨晓红, 杭文先, 秦绍刚, 刘勇兵, 刘利萍. H13钢激光熔覆钴基复合涂层的组织及耐磨性[J]. 吉林大学学报(工学版), 2017, 47(3): 891-899.
[7]	关庆丰, 黄尉, 李怀福, 龚晓花, 张从林, 吕鹏. 强流脉冲电子束诱发的Cu-C扩散合金化[J]. 吉林大学学报(工学版), 2016, 46(6): 1967-1973.
[8]	张学广, 刘纯国, 郑愿, 江仲海, 李湘吉. 基于延性损伤和剪切损伤的铝合金成形极限预测[J]. 吉林大学学报(工学版), 2016, 46(5): 1558-1566.
[9]	刘晓波, 周德坤, 赵宇光. 不同等温热处理条件下半固态挤压Mg₂Si/Al复合材料的组织和性能[J]. 吉林大学学报(工学版), 2016, 46(5): 1577-1582.
[10]	刘利萍, 刘勇兵, 姬连峰, 曹占义, 杨晓红. 原位颗粒增强钛基复合材料高温流变行为[J]. 吉林大学学报(工学版), 2016, 46(4): 1197-1201.
[11]	李春玲, 樊丁, 王斌, 余淑荣. 5A06铝合金/镀锌钢预置涂粉对接激光熔钎焊组织与性能[J]. 吉林大学学报(工学版), 2016, 46(2): 516-521.
[12]	张家陶, 赵宇光, 谭娟. 初始组织对电脉冲处理逆变奥氏体晶粒细化效果的影响[J]. 吉林大学学报(工学版), 2016, 46(1): 193-198.
[13]	张志强，贾晓飞，袁秋菊. 基于Yoshida-Uemori模型的TRIP800高强钢回弹分析[J]. 吉林大学学报(工学版), 2015, 45(6): 1852-1856.
[14]	张志强, 贾晓飞, 赵勇, 李湘吉. 高强度硼钢淬火界面热交换系数的实验与模拟[J]. 吉林大学学报(工学版), 2015, 45(4): 1195-1199.
[15]	关庆丰, 李艳, 侯秀丽, 杨盛志, 王晓彤. 固溶态Mg-Gd-Y-Nd合金强流脉冲电子束表面改性[J]. 吉林大学学报(工学版), 2015, 45(4): 1200-1205.

Metrics

Viewed

Full text

Abstract

Cited

Shared

Discussed

中碳钢温变形过程的流变应力

Flow stress of medium carbon steel under warm compression deformation

RICH HTML

PDF (PC)

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

本文评价

推荐阅读 10