吉林大学学报(工学版) ›› 2013, Vol. 43 ›› Issue (05): 1320-1324.doi: 10.7964/jdxbgxb201305028
李志杰1,2, 彭艳1,2, 刘宏民1,2, 王素芬1, 肖力子1
LI Zhi-jie1,2, PENG Yan1,2, LIU Hong-min1,2, WANG Su-fen1, XIAO Li-zi1
摘要:
为了制定中碳钢温轧工艺,利用Gleeble-3500热模拟试验机对中碳钢进行温压缩试验,研究其在不同变形温度(550~700 ℃)和应变速率(0.001~10 s-1)下的流变行为,讨论温变形过程流变应力的影响因素。研究结果表明:中碳钢温变形过程由铁素体动态回复、铁素体动态再结晶、渗碳体球化和稳态变形4个阶段构成,其软化机理主要有铁素体动态再结晶和珠光体动态球化。
中图分类号:
[1] 徐匡迪. 低碳经济与钢铁工业[J]. 钢铁, 2010, 45(3): 1-12. Xu Kuang-di. Low carbon economy and iron and steel industry[J]. Iron and Steel, 2010, 45(3): 1-12.[2] 董瀚,王毛球,翁宇庆. 高性能钢的M3组织调控理论与技术[J]. 钢铁, 2010, 45(7): 1-7. Dong Han, Wang Mao-qiu, Weng Yu-qing. Performance improvement of steels through M3 structure control[J]. Iron and Steel, 2010, 45(7): 1-7.[3] Yunusova N F, Islamgaliev R K, Bardinova M A, et al. Microstructure and mechanical properties of aluminum alloy 1421 after ECAP and warm rolling[J]. Metal Science and Heat Treatment, 2007, 49(3/4): 135-140.[4] Stolyarov V V, Zhu Y T, Alexandrov I V, et al. Grain refinement and properties of pure Ti processed by warm ECAP and cold rolling[J]. Materials Science and Engineering: A, 2003, 343(1/2): 43-50.[5] 周纪华,管克智.金属塑性变形阻力[M]. 北京: 机械工业出版社, 1989.[6] 姚圣杰,杜林秀,王国栋. 温轧低碳钢渗碳体形态对终轧组织性能的影响[J]. 材料热处理学报, 2010, 31(3): 59-63. Yao Sheng-jie, Du Lin-xiu, Wang Guo-dong. Effect of cementite morphology in a warm-rolled low-carbon steel on its microstructure and properties after finish rolling[J]. Transactions of Metals and Heat Treatment, 2010, 31(3): 59-63.[7] 熊毅,陈正阁,厉勇,等. 温压缩变形过程中渗碳体的球化行为[J]. 材料热处理学报, 2008, 29(1): 42-46. Xiong Yi, Chen Zheng-ge,Li Yong, et al. Spheroidization behavior of cementite during warm compression deformation[J]. Transactions of Metals and Heat Treatment,2008, 29(1): 42-46.[8] 谭洪锋,杨王玥,陈国安. 初始组织形态对中碳钢温变形组织演变的影响[J]. 北京科技大学学报, 2008, 30(4): 368-373. Tan Hong-feng, Yang Wang-yue, Chen Guo-an. Effect of initial microstructure on the microstructure evolution of medium carbon steel during warm deformation[J]. Journal of University of Science and Technology Beijing, 2008, 30(4): 368-373.[9] Storojeva L, Kaspar R, Ponge D. Effects of heavy warm deformation on microstructure and mechanical properties of a medium carbon ferritic-pearlitic steel[J]. ISIJ International, 2004, 44(7): 1211-1216.[10] Timokhina I B, Nosenkov A I, Humphreys A O, et al. Effect of alloying elements on the microstructure and texture of warm rolled steels[J]. ISIJ International, 2004, 44(4): 717-724.[11] 赫尔 D,培根 D. 位错导论[M]. 丁树深,李齐,译.北京: 科学出版社, 1990.[12] Solhjoo S, Ebrahimi R. Prediction of no-recrystallization temperature by simulation of multi-pass flow stress curves from single-pass curves[J]. Journal of Materials Science, 2010, 45(21): 5960-5966.[13] Suwas S, Beausir B, Tóth L S, et al. Texture evolution in commercially pure titanium after warm equal channel angular extrusion[J]. Acta Materialia, 2011, 59(3): 1121-1133.[14] Dudova N, Belyakov A, Sakai T, et al. Dynamic recrystallization mechanisms operating in a Ni-20%Cr alloy under hot-to-warm working[J]. Acta Materialia, 2010, 58(10): 3624-3632. |
[1] | 关庆丰,张福涛,彭韬,吕鹏,李姚君,许亮,丁佐军. 含硼、钴9%Cr耐热钢的热变形行为[J]. 吉林大学学报(工学版), 2018, 48(6): 1799-1805. |
[2] | 关庆丰, 董书恒, 郑欢欢, 李晨, 张从林, 吕鹏. 强流脉冲电子束作用下45#钢表面Cr合金化[J]. 吉林大学学报(工学版), 2018, 48(4): 1161-1168. |
[3] | 赵宇光, 杨雪慧, 徐晓峰, 张阳阳, 宁玉恒. Al-10Sr变质剂状态、变质温度及变质时间对ZL114A合金组织的影响[J]. 吉林大学学报(工学版), 2018, 48(1): 212-220. |
[4] | 汤华国, 马贤锋, 赵伟, 刘建伟, 赵振业. 高性能金属铝的制备、微观结构及其热稳定性[J]. 吉林大学学报(工学版), 2017, 47(5): 1542-1547. |
[5] | 关庆丰, 张远望, 孙潇, 张超仁, 吕鹏, 张从林. 强流脉冲电子束作用下铝钨合金的表面合金化[J]. 吉林大学学报(工学版), 2017, 47(4): 1171-1178. |
[6] | 杨晓红, 杭文先, 秦绍刚, 刘勇兵, 刘利萍. H13钢激光熔覆钴基复合涂层的组织及耐磨性[J]. 吉林大学学报(工学版), 2017, 47(3): 891-899. |
[7] | 关庆丰, 黄尉, 李怀福, 龚晓花, 张从林, 吕鹏. 强流脉冲电子束诱发的Cu-C扩散合金化[J]. 吉林大学学报(工学版), 2016, 46(6): 1967-1973. |
[8] | 张学广, 刘纯国, 郑愿, 江仲海, 李湘吉. 基于延性损伤和剪切损伤的铝合金成形极限预测[J]. 吉林大学学报(工学版), 2016, 46(5): 1558-1566. |
[9] | 刘晓波, 周德坤, 赵宇光. 不同等温热处理条件下半固态挤压Mg2Si/Al复合材料的组织和性能[J]. 吉林大学学报(工学版), 2016, 46(5): 1577-1582. |
[10] | 刘利萍, 刘勇兵, 姬连峰, 曹占义, 杨晓红. 原位颗粒增强钛基复合材料高温流变行为[J]. 吉林大学学报(工学版), 2016, 46(4): 1197-1201. |
[11] | 李春玲, 樊丁, 王斌, 余淑荣. 5A06铝合金/镀锌钢预置涂粉对接激光熔钎焊组织与性能[J]. 吉林大学学报(工学版), 2016, 46(2): 516-521. |
[12] | 张家陶, 赵宇光, 谭娟. 初始组织对电脉冲处理逆变奥氏体晶粒细化效果的影响[J]. 吉林大学学报(工学版), 2016, 46(1): 193-198. |
[13] | 张志强, 贾晓飞, 袁秋菊. 基于Yoshida-Uemori模型的TRIP800高强钢回弹分析[J]. 吉林大学学报(工学版), 2015, 45(6): 1852-1856. |
[14] | 张志强, 贾晓飞, 赵勇, 李湘吉. 高强度硼钢淬火界面热交换系数的实验与模拟[J]. 吉林大学学报(工学版), 2015, 45(4): 1195-1199. |
[15] | 关庆丰, 李艳, 侯秀丽, 杨盛志, 王晓彤. 固溶态Mg-Gd-Y-Nd合金强流脉冲电子束表面改性[J]. 吉林大学学报(工学版), 2015, 45(4): 1200-1205. |
|